무기계 바인더를 이용한 탄소저감형 흙포장의 성능평가 Performance Evaluation of Carbon-Reducing Soil Pavement using Inorganic Binder

유지형, 곽기봉, 김대성
  • 언어KOR
  • URLhttp://db.koreascholar.com/Article/Detail/309133
한국도로학회논문집
제17권 제6호 (2015.12)
pp.19-26
한국도로학회 (Korean Society of Road Engineers)
초록

PURPOSES: This study intends to develop an inorganic soil pavement material using industrial by-products and to evaluate its applicability as a road pavement material.
METHODS: In this study, a compressive strength experiment was conducted based on the NaOH solution molarity and water glass content to understand the strength properties of the soil pavement material according to the mixing ratio of alkali activator. In addition, the strength characteristic of the inorganic soil pavement material was analyzed based on the binder content. The performance of the soil pavement was evaluated by conducing an accelerated pavement test and a falling weight deflectometer (FWD) test.
RESULTS: As a result of the soil pavement material test based on the mixture ratio of alkali activator, it was identified that the activator that mixed a 10 M NaOH solution to water glass in a 5:5 ratio is appropriate. As a result of the inorganic soil pavement materials test based on the binder content, the strength development increased sharply when the amount of added binder was over 300 kg; this level of binder content satisfied 28 days of 18 MPa of compression strength, which is the standard for existing soil pavement design. According to the measured results of the FWD test, the dynamic k-value did not show a significant difference before or after the accelerated pavement testing. Furthermore, the effective modulus decreased by approximately 50%, compared with the initial effective modulus for pedestrian pavement.
CONCLUSIONS: Based on these results, inorganic soil pavement can be applied by changing the mixture proportions according to the use of the pavement, and can be utilized as road pavement from light load roads to access roads.

목차
1. 서론
2. 실내실험
3. 포장가속시험을 통한 성능 분석
4. 결론
감사의 글
REFERENCES
저자
  • 김대성(정회원·경일대학교 건설공학부 박사후연구원) | Kim, Dae Sung 교신저자
  • 곽기봉(경일대학교 건설공학부 박사과정) | Kawk, Gi Bong
  • 유지형(정회원·경일대학교 건설공학부 교수) | Yoo, Ji Hyeung