Spark Plasma Sintering Behavior of Binderless WC Powders KCI 등재
- 언어KOR
- URLhttps://db.koreascholar.com/Article/Detail/2290
pp.176-180
Pure WC powders which does not include a binder phase were consolidated by spark plasma sintering (SPS) process at 1600~185 for 0~30 min under 50 MPa. Microstructure alid mechanical properties of binderless WC prepared by SPS were investigated. With increasing sintering temperature, sintered density and Vickers hardness of binderless WC increased. The fracture toughness of binderless WC was 7~15 MPa depending on the sintered density and decreased with increasing the Vickers hardness. It is found that the binderless WC prepared by SPS at 175 for 10 min under 50 MPa showed nearly full densification with fine-grained structure and revealed excellent mechanical properties of high hardness (~HV 2400) and considerably high fracture toughness (~7 MPa ).