Recently with the rapid development in marine and shipbuilding industries such as marine structures, ships and chemical plants, it takes much interest in the study of corrosion fatigue characteristics that was close up an important role in mechanical design. In this study, characteristics of corner crack propagation on the base metal and heat affected zone of 5086 Al-Alloy was tested by using of a rotary bending fatigue tester and was investigated under the environments of specific resistance, σ=25Ω cm and air. The corrosion fatigue crack initiation and corrosion fatigue life sensitivity were quantitatively inspected for 5086 Al-Alloy in the specific resistance, σ=25Ω cm. Main results obtained are as follows: (1) The corrosion sensitivity of heat affected zone under specific resistance, σ=25Ωcm shows approximately 1.69~2.22 and corrosion sensitivity of base metal is more susceptible than that of heat affected zone. (2) The corrosion fatigue life sensitivity on heat affected zone decreases eminently than that of initial corrosion fatigue crack. (3) The characteristics of quarter elliptical corner crack propagation shows that depth crack is more grown than surface crack at crack initiation, but the surface crack is more propagated than depth crack as the crack propagation is increased. (4) The surface crack and depth crack growth on heat affected zone by softness show delayed phenomenon than that of base metal.