PDMS에 NaA zeolite를 0~40 wt% 가하여 PDMS-NaA zeolite 막을 제조하였다. SEM 관찰에 의하면 PDMS-NaA zeolite 막 내에 분산되어있는 NaA zeolite 입자의 크기는 2~5 μm이었다. PDMS-NaA zeolite 막의 N2와 H2 투과도는 막 내의 NaA zeolite 함량이 증가하면 증가하였고, N2보다는 H2의 투과도가 더 컸다. 그리고 PDMS-NaA zeolite 선택성(H2/N2)은 NaA zeolite 함량이 증가하면 증가하였다.

PDMS-NaA zeolite membranes were prepared by adding 0~40 wt% NaA zeolite. Based on SEM observation, NaA zeolite was dispersed in the PDMS-NaA zeolite membranes with 2~5 μm. The permeabilities of H2 and N2 gases through PDMS-NaA zeolite membranes increased as NaA zeolite contents increased and H2 gas had better permeabilities than N2. The selectivity (H2/N2) of PDMS-NaA zeolite membranes increased as NaA zeolite contents increased.