기상 화학증착법에 의해 α-Alumina 지지관 상에 제조한 Silica막의 수소투과 특성 KCI 등재

Hydrogen Permeance of Silica Membrane Prepared by Chemical Vapor Deposition Method on an α-Alumina Support Tube

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/366771
서비스가 종료되어 열람이 제한될 수 있습니다.
한국환경과학회지 (Journal of Environmental Science International)
한국환경과학회 (The Korean Environmental Sciences Society)
초록

A porous α-alumina tube of 2.5 ㎜ O.D. and 1.9 ㎜ I.D. was used as the support of an inorganic membrane. Macropores of the tube, about 150 nm in size, were plugged with silica formed by thermal decomposition of tetraethylorthosillcate at 600℃. The forced cross-flow CVD method that reactant was evacuated through the porous wall of the support was very effective in plugging macropores. The H_2 permeance of the prepared membrane was of the order of 10^-8 mol s^-1 m^-2 . Pa^-1, while the N_2 permeance was below 10^-11 mol. s^-1 . m^-2 . Pa^-1 at 600℃. This was comparable to that of silica-modified Vycor glass whose size was 4 nm.

저자
  • 김성수(지산대학 환경관리과) | Sung-Soo Kim (Dept. of Environmental Science & Technology, Jisan College)
  • 이재홍(부산대학교 화학공학과) | Jae-Hong Lee (Dept. of Chemical Engineering, Pusan National University)
  • 서동수(부산대학교 화학공학과) | Dong-Soo Suh (Dept. of Chemical Engineering, Pusan National University)
  • 박상욱(부산대학교 화학공학과) | Sang-Wook Parκ (Dept. of Chemical Engineering, Pusan National University)
  • 서봉국(구주대학 재료물리화학과) | Bong-Kuk Suh (Dept. of Materials Physics and Chemistry, Kyushu University)