The optimum polymer gel electrolyte composition ratio was 23 : 66 : 11 wt% of P(VdF-co-HFP) : PVP =20 : 3), (PC: EC =44 : 22) and TEABF4. And the optimal thickness of polymer gel electrolyte was 50um . The electrochemical characteristics result of unit cell were 31.41 Fig of specific capacitance, and 3.21x10-3 S/cm of ion conductivity. Ion conductivity of polymer gel electrolytes decreased according to added PVP through impedance analysis, and it was higher in 7 wt%, but electrochemical characteristics of unit cell were better in 3 wt% PVP. And for excellent ion conductivity of polymer gel electrolytes, the use of a thin layer electrolyte(20um) was an effective method, but with unit cell application, the best thickness was 50um . Unit cell showed higher capacitance and more stable electrochemical performance when hot pressed between polymer gel electrolyte and electrode. This results from enhancement of the physical contact between the electrode and the polymer gel electrolyte and good accessibility of the liquid electrolyte to the electrode surface.

Abstract
 1. 서론
 2. 실험 방법
  2.1. 전극 제조
  2.2. 고분자 gel 전해질의 제조 및 특성 측정
 3. 결과 및 토론
 4. 결론
 5. 참고문헌

• 정세일
• 정현철
• 강안수