Phase Analysis of Uranium Oxides by XRD After Heat Treatment

  • 언어ENG
  • URLhttps://db.koreascholar.com/Article/Detail/431063
모든 회원에게 무료로 제공됩니다.
한국방사성폐기물학회 학술논문요약집 (Abstracts of Proceedings of the Korean Radioactive Wasts Society)
한국방사성폐기물학회 (Korean Radioactive Waste Society)
초록

Once discharged, spent nuclear fuel undergoes an initial cooling process within deactivation pools situated at the reactor site. This cooling step is crucial for reducing the fuel’s temperature. Once the heat has sufficiently diminished, two viable options emerge: reprocessing or interim storage. A method known as PUREX, for aqueous nuclear reprocessing, involves a chemical procedure aimed at separating uranium and plutonium from the spent nuclear fuel. This separation not only minimizes waste volume but also facilitates the reuse of the extracted materials as fuel for nuclear reactors. The transformation of uranium oxides through dissolution in nitric acid followed by drying results in uranium taking the form of UO2(NO3)2 + 6H2O, which can then be converted into various solid-state configurations through different heat treatments. This study specifically focuses on investigating the phase transitions of artificially synthesized UO2(NO3)2 + 6H2O subjected to heat treatment at various temperatures (450, 500, 550, 600°C) using X-ray Diffraction (XRD) analysis. Heat treatments were also conducted on UO2 to analyze its phase transformations. Additionally, the study utilized XRD analysis on an unidentified oxidized uranium oxide, UO2+X, and employed lattice parameters and Bragg’s law to ascertain the oxidation state of the unknown sample. To synthesize UO2(NO3)2 + 6H2O, U3O8 powder is first dissolved in a 20% HNO3 solution. The solid UO2(NO3)2 + 6H2O is obtained after drying on a hotplate and is subsequently subjected to heat treatment at temperatures of 450, 500, 550, and 600°C. As the heat treatment temperature increases, the color of the samples transitions from orange to dark green, indicating the formation of different phases at different temperatures. XRD analysis confirms that uranyl nitrate, when heattreated at 500 and 550°C, oxidizes to UO3, while the sample subjected to 600°C heat treatment transforms into U3O8 due to the higher temperature. All samples exhibit sharp crystal peaks in their XRD spectra, except for the one heat-treated at 450°C. In the second experiment, the XRD spectra of the heat-treated UO2 consistently indicate the presence of U3O8 rather than UO3, regardless of the temperature. Under an oxidizing atmosphere within a temperature range of 300 to 700°C, UO2 can be oxidized to form U3O8. In the final experiment, the oxidation state of the unknown UO2+X was determined using Bragg’s law and lattice parameters, revealing that it was a material in which UO2 had been oxidized, resulting in an oxidation state of UO2.24.

저자
  • Seonjin Kim(Pohang University of Science and Technology (POSTECH))
  • Joohyung Kim(Hanyang University)
  • Hyejin Son(Kepco International Nuclear Graduate School (KINGS))
  • Wonpyo Jeong(Korea Nuclear International Cooperation Foundation (KONICOF))
  • Seungyeon Choi(Korea Nuclear International Cooperation Foundation (KONICOF))
  • Sangjoon Ahn(Ulsan National Institute of Science and Technology (UNIST))
  • Jaehak Cheong(Kyung Hee University)
  • Kwangheon Park(Kyung Hee University) corresponding author