AlN 분말의 고에너지 밀링에 따른 소결체의 절연 특성 KCI 등재

Insulating Behavior of Sintered AlN Ceramics Prepared by High-Energy Bead Milling of AlN Powder

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/338973
구독 기관 인증 시 무료 이용이 가능합니다. 4,000원
한국분말야금학회지 (Journal of Korean Powder Metallurgy Institute)
한국분말재료학회(구 한국분말야금학회) (Korean Powder Metallurgy Institute)
초록

Aluminum nitride (AlN) powder specimens are treated by high-energy bead milling and then sintered at various temperatures. Depending on the solvent and milling time, the oxygen content in the AlN powder varies significantly. When isopropyl alcohol is used, the oxygen content increases with the milling time. In contrast, hexane is very effective at suppressing the oxygen content increase in the AlN powder, although severe particle sedimentation after the milling process is observed in the AlN slurry. With an increase in the milling time, the primary particle size remains nearly constant, but the particle agglomeration is reduced. After spark plasma sintering at 1400℃, the second crystalline phase changes to compounds containing more Al2O3 when the AlN raw material with an increased milling time is used. When the sintering temperature is decreased from 1750℃ to 1400℃, the DC resistivity increases by approximately two orders of magnitude, which implies that controlling the sintering temperature is a very effective way to improve the DC resistivity of AlN ceramics.

목차
1. 서 론
 2. 실험 방법
 3. 결과 및 고찰
 4. 결 론
 감사의 글
 References
저자
  • 류성수(한국세라믹기술원 이천분원 엔지니어링세라믹센터) | Sung-Soo Ryu
  • 이성민(한국세라믹기술원 이천분원 엔지니어링세라믹센터) | Sung-Min Lee Corresponding Author