To improve the pyrolytic carbon (PyC) deposition rate of Carbon/Carbon (C/C) composites prepared by the traditional chemical vapor infiltration (CVI) method, the 3D Ni/wood-carbon (3D Ni/C) catalyst was introduced into the CVI process. The effects of catalyst on the density of C/C composites were studied, and the deposition rate and morphologies of PyC were investigated after catalytic CVI. The morphologies of catalyst and PyC were characterized by scanning electron microscope and polarized light microscopy. The catalytic deposition mechanism of PyC was studied by density functional theory. The experimental results show that the initial carbon deposition efficiency of the catalytic pyrolysis process was 3–4 times that of the noncatalytic process. The catalyst reduced the energy barrier in the first step of deposition reaction from 382.55 to 171.67 kJ/mol according to simulation results. The pyrolysis reaction energy with Ni catalyst is reduced by 54% than that without the catalyst.

Gabion was unfavorable to the reconstruction of the landscape caused by limit plant growth because of commonly filled with stone. Therefore, gabion was need substrate as possible to plant growth for harmonize with the surroundings and prevent of erosion. The objective of this study was to evaluate the effect of substrates based growing media containing wood meal on physical property (moisture content), chemical properties (organic matter and C/N ratio), plant cover and plant species in gabion. The substrates were composed of soil and soil mixed with growing media (9:1 (v/v) and 4:1 (v/v)). The growing media was prepared by mixing the basic materials, such as peat, perlite, with the specific materials, such as steam treated wood meal (Quercus mongolica) and NH4NO3. Field experiments were carried out on a damaged forest slope, South Korea, from January to November. The results, the moisture content of soil mixed with growing media (4:1, v/v) was maintained high value than others during the thermophilic period and consistently high organic matter which at an advantage for long term plant growth for 11 months. We were confirmed soil mixed with growing media (4:1, v/v) was an advantage to keep C/N ratio for plant growth period. The growing media based substrates has high plant cover percentage and advantage to plant growth for long term. And to conclude, in general the project is a success considering that few repairs or follow up will be necessary. This technique offers a solution to create a better harmony with the surrounding environment.

Preparation of activated carbons from wood waste including northern hardwood pins-fines and wood dust was conducted and then compared through the following methods: physical pyrolysis and CO2 activation, vacuum pyrolysis and CO2 activation, CO2 gasification, and vacuum CO2 gasification processes. Experimental results show that chars and activated carbons with high surface area and pore volume are produced from wood waste through a vacuum CO2 pyrolysis/gasification process. The effects of operation variables of vacuum pyrolysis/gasification on the properties of chars and activated carbons were investigated to identify and optimize the temperature, heating time, and heating rate. The optimized vacuum CO2 gasification conditions were found to be a temperature of 800 °C, a heating rate of 20 °C/min, and a holding time of 2 h respectively. The prepared wood-chars and activated carbons were characterized by nitrogen physisorption, scanning electron microscopy (SEM). Fourier transform infrared (FTIR) spectra determined any changes in the surface functional groups produced during different preparation stages.

최근 친환경 건축이 대두되고 있는 가운데, 목조건축물의 내진성능과 더불어 친환경 건축의 대표적 시스템으로 많은 연구가 진행되며 다시 각광을 받고 있다. 따라서 목재 구조물의 수요와 성능 개선에 관한 연구는 활발히 증가되고 있지만 목재와 같은 비균질 재료에 대한 보강법에 대한 연구는 아직 초기 수준이다. 본 연구에서는 원형단면의 목재기둥을 CFRP 시트로 보강하여 압축 및 휨 강도실험을 수행하였다. 실험 결과를 분석하여 동일한 면적에 CFRP 시트의 보강겹수와 겹침이음길이에 따른 보강효과를 나타내었다. 실험 결과 보강 시 압축 응력과 휨 응력이 증가하였다. 보강겹수와 보강재의 겹침 이음 길이의 증가에 따른 휨 응력 또한 모두 증가하는 경향을 나타내었으나, 압축응력은 목재의 비균질한 성질로 인한 횡방향 팽창이 불특정 하게 나타나 특정 경향 없이 나타나는 것을 확인하였다.

본 연구에서는 생태모방적 관점에서 목질을 천공하는 송곳벌과 밑드리좀벌의 산란관의 형태적 특징을 비교하였다. 벌목에 속하는 송곳벌과 밑드리좀벌은 목질부를 천공하는 유사한 특징이 있으나 실체현미경, 전계방사형주 사전자현미경, 광학현미경을 이용하여 산란관의 형태적 특징을 관찰한 결과 두 종 간에 큰 차이를 보였다. 송곳벌의 산란관 말단은 등쪽과 배쪽에 모두 규칙적인 돌기가 발달하여, 회전형 드릴 비트와 흡사한 형태를 띤 반면 밑드리좀벌의 산란관 말단은 한쪽 방향에만 몇 개의 돌기가 있고 다른 부분은 매끄러워 마치 톱과 비슷한 형태를 보였다. 또한 얼룩송곳벌 산란관의 말단은 대칭적으로 4 등분으로 되어있다가 14번째 돌기를 지나면서 2 : 1 : 1의 비율로 3등분이 되는 반면, 밑드리좀벌 산란관의 말단은 2 : 1 : 1의 비율로 3등분되어 있음을 확인할 수 있었다. 또한, 송곳벌의 산란관의 중간을 수평으로 자른 단면구조에 서는 dovetail joint의 구조가 확인되었으며, 이를 통해 천공을 위해 수직 운동을 한다는 것을 확인할 수 있었다. 이러 한 두 종의 형태적 차이는 목질 부분을 먹이원으로 이용하는 송곳벌과 벌의 유충을 이용하는 밑드리좀벌의 생활방 식뿐만 아니라 계통분류학적 차이에 의해 기인한 것으로 사료된다. 끝으로, 산란관 말단 부분의 성분분석결과 두 종 모두에서 높은 강도의 특성을 부여하는 아연이 검출되었다. 이는 주로 목질을 천공하는 두 종의 생태적 적응 과정에 의하여 특이적으로 진화된 것으로 사료된다.

본 연구에서는 소나무재선충을 매개하는 매개충 솔수염하늘소와 북방수염하늘소에 대하여 무인항공기(무인헬리콥터)를 이용하여 유인항 공용 방제 약제의 약효 및 약해를 조사하였다. 약효는 소나무와 잣나무의 수간을 3등분한 곳에 대상 곤충을 케이지에 넣어 매달아 두어 살충효과 를 조사하였다. 시험약제로는 티아클로프리드 액상수화제, 아세타미프리드 미탁제, 플루피라디퓨론 액제를 각각 33배로 희석하여 살포하였고, 감수지를 이용하여 살포 약제의 낙하입자를 측정하고 피복도를 조사하였다. 약제 살포에 의한 주변 비산거리 및 비산량을 조사하였다. 세 약제 모 두 솔수염하늘소, 북방수염하늘소에 대하여 96%이상의 우수한 살충 효과를 보였다. 낙하입자 분석 결과 낙하입자는 균일한 양상을 보였다. 주변 비산 현상 분석 결과, 약제 살포시 무인헬리콥터 진행방향으로 20 m의 비산을 보였고, 좌우, 후방으로 10 m의 비산이 확인되었다. 낙하입자수에 의한 비산량 조사 결과, 모든 방향에서 5 m내에서 낙하입자지수 6-7이였고, 10 m지점에서는 낙하입자지수 2를 기록하였다.

In this study, an experimental study was carried out to evaluate the bond shear performance according to the shear connector between the glue-laminated timber and steel interface. Ten block shear specimens were fabricated according to the configuration of the adhesive surface of wood and steel. In addition, four test specimens were produced according to the main variable shape of the wood-concrete shear connector. As a result of the block shear test, the shear strength of the steel-wood adhesive is shown to have a shear performance greater than the wood-wood shear strength. As a result of the push-out test according to the shape of the shear connector, the shear strength increased linearly with the attachment area. The complete composite behavior between the glued-laminated timber and the steel can be secured.