SPG (Shirasu porous glass) 관형 막이 설치된 회분식 막유화 장치를 사용하여 이온성 약물이 담지된 단분산 polycaprolactone (PCL) 마이크로캡슐을 제조하기 위한 막유화 공정변수의 최적조건을 결정하였다. 마이크로캡슐에 담지된 이온성 약물로는 양이온성인 lidocaine-hydrochloride, 중성인 sodium salicylate와 음이온성인 4-acetaminophen의 3가지를 사용하였으며, PCL 마이크로캡슐로부터 이들 모델약물의 방출거동을 검토하였다. 캡슐제조에 사용된 PCL의 농도와 분자량, 막간 압력차, 분산상과 연속상에 첨가시킨 유화제의 농도, 연속상의 교반속도가 막유화법으로 제조된 PCL 캡슐의 크기와 크기분포에 미치는 영향을 검토하였다. 이들 공정변수의 조절을 통해 평균 크기 약 5 μm의 균일한 마이크로캡슐을 제조할 수 있었다. 약물 방출실험 결과 산성조건에서 알칼리조건으로 방출환경이 변화됨에 따라 약물 방출속도가 증가하였다.

Fe(C) nanocapsules were prepared by the chemical vapor condensation(CVC) process using the pyrolysis of iron Their characterizations were studied by means of X-ray diffraction, X-ray photoelectron spectrometer and transmission electron microscopy. The long-chained Fe(C) nanocapsules hav-ing the mean size of under 70 nm could be obtained below in different gas flow rates. The particle size of the powders was increased with increasing decomposition temperature, but it was decreased with increasing CO gas flow rate. The Fe powders produced at consisted of three layers of phases, but it had two phase core-shell structure which consited of phase of core and graphite of shell at

곤충병원선충(Steinernema carpocapsae)을 이용한 지상부 가해 해충 방제는 자외선과 건조 등의 제약점 때문에 적용의 한계를 갖고 있다. 본 연구는 이를 극복하기 위한 방제 기술을 개발하는 데 목적을 두고, 기주의 지상부를 가해하는 두 나비목 해충인 파밤나방(Spodoptera exigua)과 담배거세미나방(Sp. litura)을 대상으로 실시하였다. 감염태 선충을 포함하는 알지닌캡슐은 이들 두 해충에 대해 뚜렷한 섭식독성을 보였다. 이러한 독성은 캡슐내에 함유되어 있는 감염태 선충의 밀도에 따라 증가하는 전형적인 양독곡선을 나타냈다. 캡슐내에 잔존하는 수분함량은 감염태 선충의 생존력에 가장 중요한 요인으로 작용했다. 캡슐내에 약 10%이상의 수분이 함유되었을 때 약 80%의 감염태 선충이 생존하였다. 캡슐내 보습 능력은 상대습도, 온도 및 캡슐의 크기에 따라 변동되나, 캡슐 형성 과정 중의 시트릭산 반응 시간과는 무관하였다. 알지닌캡슐이 15 증류수에 보관되었을 때, 60일 경과후에도 80%이상의 생존 능력을 보였다. 이러한 감염태 선충이 함유된 캡슐을 섭식유도제로서 사용된 파추출물을 함유시킨 후 야외 땅콩을 가해하는 파밤나방 3령충에 적용시켰을 때, 약 90%의 방제 효과를 나타냈다. 이러한 결과는 알지닌캡슐이 곤충병원선충의 저장 형태의 캡슐 용도 뿐만 아니라 지상부 해충 방제용 제제화로서 이용될 수 있다고 제시한다.

The Sn - graphite composites were prepared by chemical encapsulation method for anode materials in Li-ion batteries. EDS and XRD analysis confirmed the presence of Sn in the graphite structure. Cyclic voltammometry (CV) measurement shows extra reduction and oxidation peaks, which might to be related to the formations of alloy compounds. Graphite-tin composite electrodes demonstrated higher Lithium storage capacities than graphite electrodes. Due to the nature of fine Sn particles on graphite surface, the graphite-tin composite electrodes have shown a good cycle properties.

We investigated the property of formation of mono-vesicle(designated nano-some) with using of the combined co-emulsifiers and phospholipid. Nano-some was prepared with hydrogenated lecithin(HL) and diethanolamine cetyl phosphate(DEA-CP) by swelling reaction. Kojic acid and kojic dipalmitate could be made stabilization by nano-some system using microfluidizer(MF). Nano-some has a good affinity to skin by means of this system. The composition was compounded by 2% of hydrogenated lecithin (phosphatidyl choline contained with 75%, 0.5% of DEA-CP and 0.5% of diglyceryl dioleate (DGDO). To make nano-some, several conditions of MF have to be considered as follows. The optimum pH was 6.0. The pressure was 10,000psi and passage temperature was at 306℃. The nano-some base was passed to homogenize continually 3 times through MF. The Particle size distributions of the vesicles were with in 57~75.7nm(mean 66nm) by measuring the Zetasizer-3000. Zeta potential of vesicles with 3 times passage through MF was -24.8mV. Formations for nano-some vesicle certificated photograph by scanning electric magnification (SEM). Stability of nano-some was very good for 6months. The turbidity was very good transparency compared nano-some with liposome. It was formed the mono vesicle in the opposite direction to be formed the multi-lamellar vesicle of liposome.

본 연구에서는 보수 모르타르와 직접 혼합 가능한 결정성장형 자기치유 고상캡슐을 제조하였으며, 자기치유 고상캡슐이 혼합된 보수 모르타르의 품질 및 균열 치유 성능 특성을 평가하였다. 자기치유 고상캡슐을 혼합한 보수 모르타르의 테이블 플로우 및 공기량 평가 결과 혼합율에 관계없이 테이블 플로우 및 공기량은 큰 영향이 없는 것으로 나타났다. 압축강도는 캡슐 혼합율이 증가할수록 강도가 감소하는 경향이 나타났다. 정수위 투수시험에 따른 균열 치유 특성 평가 결과 초기 투수량이 감소하는 결과가 나타났으며, 시간 경과에 따라 반응 생성물 발생하여 균열이 치유되는 것을 확인 할 수 있었다.

In this paper, water flow test was performed to evaluate the healing performance of self - healing solid capsules based on inorganic materials. The water flow test was used to evaluate the permeability reduction for each healing age with respect to the initial permeability of crack - induced test specimens.

본 연구에서는 시멘트 복합재료와 직접 혼합 가능한 자기치유 마이크로 캡슐을 제조하였으며, 자기치유 마이크로 캡슐이 혼합된 시멘트 복합재료의 품질 및 균열 치유 성능 특성을 평가하였다. 종래의 경우 자기치유 캡슐 제조와 균열 치유 특성 평가에만 치중되어 평가되어 왔다. 따라서 자기치유 마이크로 캡슐은 시멘트 복합재료와 혼합시 시멘트 복합재료의 품질에 미치는 영향이 있기 때문에 이에 대한 검토를 수행하였다. 자기치유 마이크로 캡슐을 혼합한 시멘트 복합재료의 테이블 플로우 및 공기량 평가 결과 혼합율에 관계없이 테이블 플로우 및 공기량은 큰 영향이 없는 것으로 나타났다. 압축강도 및 쪼갬인장강도는 캡슐 혼합율이 증가할수록 강도가 감소하는 경향이 나타났다. Water Flow에 따른 균열 치유 특성 평가 결과 초기 투수량이 감소하는 결과가 나타났으며, 시간 경과에 따라 반응 생성물 발생하여 균열이 치유되는 것을 확인 할 수 있었다.