Adhensively bonded joints in dissimilar materials have been widely applied in various engineering fields such as automobiles, space vehicle, semiconductor, vessel. To establish a fracture criterion and a reasonable strength evaluation method on adhensively interfaces in dissimilar materials, it is necessary to assess fracture parameters with various bonding conditions. In this paper, through stress analysis by using the 2-dimensional elastic boundary element method(BEM), the stress singularity factors on adhensively bonded joint in dissimilar materials were investigated quantitatively, and suggested the strength evaluation method by using fracture parameters

Cu-brazed layer between the sintered-cam(Fe-5Cr-lMo-0.5P-2.5C, wt%) and seamless steelpipe(0.25-0.35C, 0.3-1.0 Mn, bal Fe, wt%) in the camshaft shows a columnar structure of -phase growing from the steel pipe. Liquid phase sintered 60Fe-40Cu alloys are carburized to simulate the brazing process giving rise to the columnar growth. Liquid film migrations and columnar growth of -grains are observed in the carburized regions. The -grains grow in the same direction as the C-diffusion. Fe-solubility in the liquid of carburized region is higher than in the uncarburized by about 0.3 at%. The columnar growth is driven by the gradient of the supersaturated Fe-solute in the liquid between two adjacent -grains.

이종재 마찰용접재 강도특성과 초음파 반사계수와의 상관성에 관하여 실험적으로 연구한 결과의 요약은 다음과 같다. 1. 이종재 마찰용접 이음면에서의 초음파 반사계수를 펄스반사법에 의하여 측정산출할 수 있다. 2. 5MHz의 비교적 낮은 주파수의 탐촉자를 사용하므로써 시험편의 표면가공 오차를 무시할 수 있다. 3. 알루미늄과 스테인레스의 마찰용접에서는 용접조건으로 마찰가열시간이나 가열압력을 변수로 하였을 때보다 업셋가압력을 변수로 하였을 때 반사계수의 변화가 뚜렷하다. 4. 업셋가압력을 변수로 한 용접조건과 반사계수사이에는 선형적 상관관계가 있다. 5. 용접이음면에서의 이음인장강도와 반사계수와의 상관관계식을 정량적으로 도출할 수 있다. 6. 초음파 반사계수에 의해 이종재 마찰용접 품질의 비파괴적 평가가 가능하다