As a growth-template of ZnO nanorods (NR), a hexagonal β-Ni(OH)2 nanosheet (NS) was synthesized with the low temperature hydrothermal process and its microstructure was investigated using a high resolution scanning electron microscope and transmission electron microscope. Zinc nitrate hexahydrate was hydrolyzed by hexamethylenetetramine with the same mole ratio and various temperatures, growth times and total concentrations. The optimum hydrothermal processing condition for the best crystallinity of hexagonal β-Ni(OH)2 NS was determined to be with 3.5 mM at 95˚C for 2 h. The prepared Ni(OH)2 NSs were two dimensionally arrayed on a substrate using an air-water interface tapping method, and the quality of the array was evaluated using an X-ray diffractometer. Because of the similarity of the lattice parameter of the (0001) plane between ZnO (wurzite a = 0.325 nm, c = 0.521 nm) and hexagonal β-Ni(OH)2 (brucite a = 0.313 nm, c = 0.461 nm) on the synthesized hexagonal β-Ni(OH)2 NS, ZnO NRs were successfully grown without seeds. At 35 mM of divalent Zn ion, the entire hexagonal β-Ni(OH)2 NSs were covered with ZnO NRs, and this result implies the possibility that ZnO NR can be grown epitaxially on hexagonal β-Ni(OH)2 NS by a soluble process. After the thermal annealing process, β-Ni(OH)2 changed into NiO, which has the property of a p-type semiconductor, and then ZnO and NiO formed a p-n junction for a large area light emitting diode.

As a pore precursor, carbon black with different content of 0 to 60 vol% were added to (Ba,Sr) powder. Porous (Ba,Sr) ceramics were prepared by pressureless sintering at for 1h under air. Effects of carbon black content on the microstructure and PTCR characteristics of porous (Ba,Sr) ceramics were investigated. The porosity of porous (Ba,Sr) ceramics increased from 6.97% to 18.22% and the grain size slightly decreased from to with increasing carbon black contents. PTCR jump of the (Ba,Sr) ceramics prepared by adding carbon black was more than , and slightly increased with increasing carbon black. The PTCR jump in the (Ba,Sr) ceramics prepared by adding 40 vol% carbon black showed an excellent value of , which was above two times higher than that in (Ba,Sr) ceramics. These results correspond with Heywang model for the explanation of PTCR effect in (Ba,Sr) ceramics. It was considered that carbon black is an effective additive for preparing porous based ceramics. It is believed that newly prepared (Ba,Sr) cermics can be used for PTC thermistor.

Sintered Nd-Fe-B magnets are widely used in many fields such as motors, generators, actuators, microwaves and so on due to their excellent magnetic properties. Many researchers have shown that the Nd-rich phase was essentially important for high magnet properties. In this study, we focused on controlling of the Nd-rich phase to enhance magnetic properties by the cyclic sintering process. Nd-Fe-B based sintered magnets were prepared by isothermal sintering and cyclic sintering processes. Magnetic properties and microstructure of the magnets were investigated. The coercivity was enhanced from 21.2 kOe to 23.27 kOe after 10 cycles of the sintering. The Nd-rich phase was effectively penetrated into the grain boundary between the grains by the cyclic sintering.

Several species of the genus Aphidius are used in biological control programs against aphid pests throughout the world and their behavior and physiology are well studied. While the importance of sensory organs in their behavior is understood, their antennal structure remains largely unknown. In this study, the external morphology and distribution of the antennal sensilla on the antennal of both female and male adults of A. colemani were described using scanning electron microscopy (SEM). Generally, the filiform antennae of males (1,515.2±116.5 ㎛) are longer than females (1,275.1±103.4 ㎛). Antennae of this species are made up of radicle, scape, pedicel and flagellomeres. Male and female antennae differed in the total number of flagellomeres as 15 in males and 13 in females. The result of SEM observation was characterization and grouping of seven types of receptors into morphological classes: Bohm bristles, Sensilla placodea, 2 types of S. coeloconica and S. trichodea, and S. basiconica as with a tip pore and with wall pores. In addition, the possible functions of the above sensilla types are discussed in light of previously published literature, mechanoreception (Bohm bristles, S. coeloconica Ⅰ & Ⅱ and S. trichodea) and chemoreception (S. placodea, S. basiconica type Ⅰ & Ⅱ).

The microstructure and positive temperature coefficient of resistivity (PTCR) characteristics of 0.1mol%Na2Ti6O13doped 0.94BaTiO3-0.06(Bi0.5Na0.5)TiO3 (BBNT-NT001) ceramics sintered at various temperatures from 1200oC to 1350oC wereinvestigated in order to develop eco-friendly PTCR thermistors with a high Curie temperature (TC). Resulting thermistors showeda perovskite structure with a tetragonal symmetry. When sintered at 1200oC, the specimen had a uniform microstructure withsmall grains. However, abnormally grown grains started to appear at 1250oC and a homogeneous microstructure with large grainswas exhibited when the sintering temperature reached 1325oC. When the temperature exceeded 1325oC, the grain growth wasinhibited due to the numerous nucleation sites generated at the extremely high temperature. It is considered that Na2Ti6O13 isresponsible for the grain growth of the 0.94BaTiO3-0.06(Bi0.5Na0.5)TiO3 ceramics by forming a liquid phase during the sinteringat around 1300oC. The grain growth of the BBNT-NT001 ceramics was significantly correlated with a decrease of resistivity.All the specimens were observed to have PTCR characteristics except for the sample sintered at 1200oC. The BBNT-NT001ceramics had significantly decreased ñrt and increased resistivity jump with increasing sintering temperature at from 1200oC to1325oC. Especially, the BBNT-NT001 ceramics sintered at 1325oC exhibited superior PTCR characteristics of low resistivityat room temperature (122Ω·cm), high resistivity jump (1.28×104), high resistivity temperature factor (20.4%/oC), and a highTc of 157.9oC.

The evolution of sinterability, microstructure and mechanical properties for the spark plasma sintered(SPS) Ti from commercial pure titanium(CP-Ti) was studied. The densification of titanium with 200 mesh and 400 mesh pass powder was achieved by SPS at under 10 MPa pressure and the flowing +Ar mixed gas atmosphere. The microstructure of Ti sintered up to consisted of equiaxed grains. In contrast, the growth of large elongated grains was shown in sintered bodies at with the 400 mesh pass powder and the lamella grains microstructure had been developed by increasing sintering temperature. The Vickers hardness of 240~270 HV and biaxial strength of 320~340 MPa were found for the specimen prepared at .

A hierarchical computational method has been developed and used with finite element method based on dislocation density multiple-slip crystalline formulation to predict how nanoindentation affects behavior in face-centered cubic crystalline aggregates. Using displacement profiles which were obtained from molecular dynamics(MD) nanoindentation simulation, scaling relations based on indentation depths, grain-sizes, and grain aggregate distributions were obtained. These relations then applied to coarsen grains in micros- tructurally based FE formulation which accounts for dislocation density evolution, crystalline structures. This computational regime was validated with a several experimental results related to single gold crystals. This hierarchical model provides a tool to link nanosacle level with a microstructurally based FEM formulation that can be to ascertain inelastic effects such as dislocation density evolution. With the above certainty temperature distribution during the nanoindentation simulation also was investigated along with the different indentation depth.

The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. -SiC powder with 0, 2, 6, 10 wt% of -SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at for 10 min. The heating rate, applied pressure and sintering atmosphere were kept at , 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of -SiC seeds into -SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the -SiC seeds added in -SiC, the rate of grain growth decreased with -SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.

The polarizing images of hard tissues including bone and cementum show characteristic features of different birefringence fortheir microstructures. Nevertheless, the clear mechanism of the amplified birefringence under polarizing microscope has not been well understood. We hypothesized that the unique polarized light could be accumulated in the microtubules due to the decreased refractory angle by the inside lower-density matrix, and then the accumulated light in the microtubules could be dispersed brightly. In order to elucidate the polarizing effect on the microtubules, the dentinal tubules in different conditions were observed, and compared with each other to explain their birefringence phenomena. In the decalcified sections of normal tooth, the dentinal tubules located near the pulp chamber showed strong birefringence, while the sclerosed dentinal tubules near the dentino-enamel junction did not show the birefringence. The birefringence was more conspicuous in the longitudinal sectionsof dentinal tubules than in the cross sections. In the decalcified sections of complex odontoma, which produced abnormal and immature dentinal tubules, the birefringence was not observed in the shrunken dentinal tubules filled with dense materials, while the peritubular matrix showed clear birefringence. The birefringence was also observed in the collagen fibers in the connective tissue, and continuously strong in the immature cemental materials containing precollagen fibers. However, the highly mineralized osteodentine did not show the birefringence. Taken together, these data suggest that the microtubules composed ofless-dense matrix than the background tissue, i.e., dentinal tubules, Haversian canals, etc., produce the amplified birefringence by the polarizing light according to the hypothesis of microtubule refraction.

Glass ceramics were made from coal bottom ash by adding CaO and Li2O as glass modifiers and TiO2 as a nucleating agent in a process of melting and quenching followed by a thermal treatment. The surface of the glass ceramics has 1.6 times more Li2O compared to the inner matrix. When TiO2 was not added or when only 2 wt% was added, the surface parts of the glass ceramics were crystalline with a thickness close to 130μm. In addition, the matrixes showed only the glass phase and not the crystalline phase. However, doping of TiO2 from 4 wt% to 10 wt% began to create small crystalline phases in the matrix with an increase in the quantity of the crystalline. The matrix microstructure of glass ceramics containing TiO2 in excess of 8 wt% was a mixture of dark-gray crystalline and white crystalline parts. These two parts had no considerable difference in terms of composition. It was thought that the crystallization mechanism affects the crystal growth, direction and shape and rather than the existence of two types of crystals.

The influence of various surface morphologies on the mechanical strength of silicon substrates was investigated in this study. The yield for the solar cell industry is mainly related to the fracturing of silicon wafers during the manufacturing process. The flexural strengths of silicon substrates were influenced by the density of the pyramids as well as by the size and the rounded surface of the pyramids. To characterize and optimize the relevant texturing process in terms of mechanical stability and the fabrication yield, the mechanical properties of textured silicon substrates were investigated to optimize the size and morphology of random pyramids. Several types of silicon substrates were studied, including the planar type, a textured surface with large and small pyramids, and a textured surface with rounded pyramids. The surface morphology and a cross-section of the as-textured and fractured silicon substrates were investigated by scanning electron microscopy.

Sintered Nd-Fe-B magnets have been widely used due to their excellent magnetic properties, especially for driving motors of hybrid and electric vehicles. The microstructure of Nd-Fe-B magnets strongly affects their magnetic properties, in particular the coercivity. Therefore, a post-sintering process like heat-treatment is required for improving the magnetic properties of Nd-Fe-B sintered magnets. In this study, cyclic heat treatment was performed at temperatures between and up to 16 cycles in order to control microstructures such as size and shape of the Nd-rich phase without grain growth of the phase. The 2 cycles specimen at this temperature range showed more homogeneous microstructure which leads to higher coercivity of 35 kOe than as-sintered one.

Hydrogen production via high high-temperature steam electrolysis consumes less electrical energy than compared to conventional low low-temperature water electrolysis, mainly due to the improved thermodynamics and kinetics at elevated temperaturetemperatures. The elementalElemental powders of Cu, Ni, and YSZ are were used to synthesize high high-temperature electrolysis cathodecathodes, of Ni/YSZ and Cu/YSZ composites, by mechanical alloying. The metallic particles of the composites were uniformly covered with finer YSZ particles. Sub-micron sized pores are were homogeneously dispersed in the Ni/YSZ and Cu/YSZ composites. In this study, The cathode materials were synthesized and their Characterizations properties were evaluated in this study: It was found that the better electric conductivity of the Cu/YSZ composite was measured improved compared tothan that of the Ni/YSZ composite. Slight A slight increase in the resistance can be produced for in a Cu/YSZ cathode by oxidation, but it this is compensated offset for by a favorable thermal expansion coefficient. Therefore, Cu/YSZ cermet can be adequately used as a suitable cathode material of in high high-temperature electrolysis.

Thermally evaporated 10 nm-Ni/1 nm-Au/(30 nm-poly)Si structures were fabricated in order to investigate the thermal stability of Au-inserted nickel silicide. The silicide samples underwent rapid thermal annealing at 300~1100˚C for 40 seconds. The sheet resistance was measured using a four-point probe. A scanning electron microscope and a transmission electron microscope were used to determine the cross-sectional structure and surface image. High-resolution X-ray diffraction and a scanning probe microscope were employed for the phase and surface roughness. According to sheet resistance and XRD analyses, nickel silicide with Au had no effect on widening the NiSi stabilization temperature region. Au-inserted nickel silicide on a single crystal silicon substrate showed nano-dots due to the preferred growth and a self-arranged agglomerate nano phase due to agglomeration. It was possible to tune the characteristic size of the agglomerate phase with silicidation temperatures. The nano-thick Au-insertion was shown to lead to self-arranged microstructures of nickel silicide.

본 연구에서는 내분비계 장애물질으로 알려져 있고, 플라스틱 제품의 가소제로 사용되고 있는 di-(2-ethylhexyl) phthalate (DEHP)가 흰쥐의 간세포 미세구조와 간조직내 metallothionein (MT)의 발현 양상에 미치는 영향을 조사하였다. DEHP는 흰쥐 간세포의 미세구조와 MT 발현에 영향을 주었다. 실험군의 경우 조면소포체가 발달하고, 미토콘드리아가 증가하며 리소솜 혹은 퍼옥시좀들이 증가하는 경향을 나타냈다. 한편, MT