In this study, mock-up test of ternary blended concrete using structure was conducted in order to evaluate the temperature rise. The results of the mock-up test, it was found that it was convenient to obtain the minimum temperature rise of 3:5:2 mixing.

Recently, a Multi-Walled Carbon Nano Tube(MWCNT) is widely used to increase mechanical strength of the cementitious composite material. In this study, a dilution of MWCNT aqueous solution(from wt 2.0%, 1.5% to wt 1.0%) is a main parameter. A compressive strength of diluted CNT cement mortar is maximum 4.7% larger than that of a pure CNT cement mortar. The result indicates that the diluted MWCNT aqueous solution of the MWCNT cement mortar makes very little differences of the compressive strength.

In this study, hydration heat analysis of ternary blended concrete using mock-up structure was conducted in order to evaluate the temperature rise and crack index. The results of the analysis of hydration heat, it was found that it was convenient to obtain the minimum crack index and temperature rise of 3:5:2 mixing.

This study evaluated the standard consistency, setting time, hydration heat, and compressive strength of binary blended cement concrete (general and high strength) using air cooled ladle furnace slag (LFS) of 3, 5, 7, 10wt.% as an admixture for ordinary portland cement (OPC). Results showed that binary blended cements using the LFS of lower than 5wt.% shortened the setting time and reinforced the compressive strength of concrete (general and high-strength) compared to OPC concretes although binary blended cements needed more water to achieve the standard consistency. This indicated that LFS could be used as a useful admixture for manufacturing binary blended cement. Thus, we expected that the upcycling of LFS would be contributed to save energy consumption and reduce the greenhouse gas emission from the field of cement industry.

This paper presents an experimental investigation in order to evaluate fresh and hardened properties of LP (Limestone Powder) blended cement concrete. The cement contents of the mixtures are replaced by LP in the range of 10%, 15%, 25%, and 35%, while a control mixture is prepared with only OPC (Ordinary Portland Cement). The fresh concrete properties like slump and air content are similar to those of control mixture up to 35% of replacement ratio of LP, however a delay in setting time is evaluated. The hardened properties including compressive strength, flexural strength, and rapid freezing and thawing resistance shows similar results of control mixture up to 15% of replacement. Relatively lower strength development is evaluated over 25% replacement of LP. For accelerated carbonation test, resistance to carbonation rapidly decreases with increasing LP replacement ratio due to the limited amount of Ca(OH)2. From the study, LP replacement under 15% can be adopted considering reduction of strength and resistance to carbonation.

In this study, the hydration characteristics of low heat concrete with respect to the binder type are investigated experimentally. According to research results, TBC(Ternary Blended Cement)1, 2 applied low heat concrete, the heat of hydration was found to be reduced and the 28 days compressive strength was superior to that of FAC(Fly Ash Cement).

본 연구는 초고강도콘크리트의 배합에 사용되는 3성분계 혼합시멘트의 최적조합을 도출하기 위한 실험연구이다. 3성분계 혼합시멘트는 포틀랜드시멘트, 고로슬래브 미분말 0%, 30%, 40%, 50% 및 플라이애시 0%, 10%, 20%, 30%로 구성하였다. 물결합재비 0.18의 초고강도콘크리트를 대상으로 각 실험체의 압축강도와 공극구조를 조사한 결과, 플라이애시 10%, 고로슬래그 미분말 30%를 혼합한 3성분계 혼합시멘트를 사용한 콘크리트의 압축강도는, 50nm 이상의 공극량 감소에 의해, Plain 콘크리트에 비해 현저히 증가하였다.

최근들어 백두산 지역의 지표면 팽창현상이 관찰되면서, 백두산의 분화 위험성이 증대되고 있다. 화산이 분화하는 경우, 무수한 화산재의 비산으로 항공, 교통, 물류, 정밀기계 산업 등이 큰 타격을 입게 될 뿐만 아니라, 화산재의 처리 및 처분에도 막대한 국가적 손실이 발생하므로 화산재 처리 및 활용방안의 개발이 절실히 요구된다. 본 연구에서는 화산재를 건설재료로 활용하기 위하여 백두산, 한라산의 화산재 및 다공성의 제올라이트에 시멘트 및 메타카올린을 첨가한 공시체에 대한 재령 0일 및 7일의 배합비별 압축강도 특성을 분석하였다. 실험 결과, 재령 7일에 대하여 혼합재(화산재 및 제오라이트), 시멘트 및 메타카올린의 비율을 3.5：1：0.1로 배합한 경우 최대의 압축강도를 나타내었으며, 재령 및 단위시멘트량의 증가, 메타카올린의 첨가가 압축강도 특성에 큰 영향을 미치는 것으로 나타났다.

2002년에 백두산 지역을 중심으로 강진에 의한 지표면 팽창현상이 관찰되면서, 백두산의 화산폭발 가능성이 높아지고 있다. 이에 따라, 그동안 국내에서 재난유형으로 별도의 분류가 없던 화산폭발에 대한 대책이 정부차원에서 논의되기 시작하였다. 화산폭발이 발생하면 무수한 화산재가 각종 사회기반시설을 덮게 되며, 비산에 의해 항공, 물류, 정밀기계산업 등에 타격이 발생하게 된다. 본 연구에서는 화산재를 건설재료로 활용하기 위하여 백두산, 한라산의 화산재 및 다공성의 제올라이트에 시멘트 및 메타카올린을 첨가한 재령 7일의 공시체에 대한 배합비별 동결융해 저항성을 분석하였다. 실험 결과, 재령 7일에 대하여 혼합재(화산재 및 제오라이트), 시멘트 및 메타카올린의 비율을 3.5：1：0.1로 배합한 경우 동결융해 저항성이 가장 우수한 것으로 나타나, 재령 및 단위시멘트량의 증가, 메타카올린의 첨가가 동결융해 저항성에 큰 영향을 미치는 것으로 나타났다.

본 연구는 실리카 퓸의 대체율을 4단계(시멘트 중량의 0, 5, 10 및 15%)로 달리하여 제조한 시멘트 모르타르의 황산마그네슘 침식 저항성을 평가하며, 침식에 의한 성능저하 원인을 조사하기 위하여 수행되었다. 실리카 퓸 혼합 모르타르를 5% 황산마그네슘 용액에 360일 동안 침지한 후, 재령별 압축강도 및 팽창을 측정하였으며, XRD, SEM 및 DSC와 같은 여러 기기분석법을 활용하여 침식에 의한 시멘트 경화체의 성능저하 원인을 고찰하였다. 실험 결과에 의하면, 실리카 퓸을 혼합한 시멘트 경화체의 황산마그네슘 침식은 주로 gypsum, thaumasite 및 brucite 등의 반응생성물과 깊은 관련이 있는 것으로 나타났다.

연구는 알칼리 활성시멘트(Alkali Activated Cement)를 콘크리트에 활용하기 위한 기초적인 연구로서 잔골재 및 굵은골재의 혼합비는 일정하게 하고, 활성화제/플라이 애쉬의 혼합비, 그리고 활성화제 중 물유리, 수산화나트륨, 물의 혼합비를 변화시킨 AAC 콘크리트에 대한 압축강도를 측정하였다. 또한 각 변수에 따른 압축강도의 특성을 분석하고, AAC 콘크리트의 최적 혼합비를 구하였다. 그 결과 최대 압축강도 발현을 위한 활성화제 중 물유리, 수산화나트륨, 물의 최적 혼합비는 4.0:1.0:2.5 이었으며, 활성화제/플라이 애쉬의 최적 혼합비는 0.7 이었다

본 연구는 실리카 퓸을 사용한 시멘트 경화체의 황산염침식 저항성을 평가하기 위하여 수행되었다. 실리카 퓸을 시멘트 중량에 대하여 0, 5, 10 및 15%의 4단계로 대체한 모르타르 및 0 및 10%의 2단계로 대체한 페이스트를 제조하여 침지실험을 실시하였다. 황산나트륨용액에 510일 동안 모르타르 및 페이스트를 침지한 후 재령별 외관조사, 팽창, 압축강도 감소율 및 공극특성을 조사한 결과, 실리카 퓸 대체율에 관계없이 실리카 퓸을 대체한 시멘트 경화체는 황산염침식에 대하여 저항성이 매우 우수하였으나, 보통포틀랜드시멘트 모르타르 및 페이스트는 황산염침식에 의한 극심한 성능저하 현상이 관찰되었다.