This study deals with improvement plans and application results to improve the safety of secondary batteries and chargers applied to Tactical Multi-band Multi-role Radio(TMMR), a new military communication equipment. Due to the nature of the portable weapon system, the terminal structure and manufacturing process of the battery and charger were improved to strengthen resistance to vibration and shock generated during movement, and the battery structure was partially changed to secure resistance to mechanical shock generated when the charger was coupled. In addition, retrospective application was completed for all secondary batteries and chargers previously delivered for TMMR, helping the Korean military to operate next-generation radios in a safer environment.

리튬2차전지용 양극소재 개발을 위해 Li[L ixM n1-x-yC ry ] O2를 공침법(co-p.ecipitation method)을 적용하여 각각 650℃(CR650)와 850℃(CR850)에서 합성하였다. 리트벨트 구조분석 결과 계산의 정밀도를 나타내는 R 지수값을 보면 Rexp에 대한 Rwp값( Rwp/ Rexp)은 CR650과 CR850의 각각에 대해 19.2%/10.1%과 15.9%/9.76%를 보여주며, Rb값은 각각 10.9%와 8.54%, 그리고 S(GofF)값은 각각 1.9와 1.6으로 계산되었다. 합성된 양극소재는 공간군 R3m의 층상구조(LiMn O2)가 존재하였으며, 전이금속 층 내의 Mn이 Li로 치환되면서(Li[L i13/M n23/] O2) 단사구조(C2/c)의 거대격자(Superlattice) 구조현상도 관찰되었다. 계산된 단위포는 공간군 R3m, CR650이 a=2.8520(2)a, c=14.248(2)a, V=100.40(1)a3이며, CR850은 a=2.8504(1)a, c=14.2371(7)a, V=100.179(8)a3으로 각각 계산되었다. 또한 최종 결정된 화학식은 CR650은 Li[L i0.35M n0.56C r0.09] O2, CR850은 Li[L i0.27M n0.61C r0.13] O2으로 각각 구해졌다.다...다..구해졌다.다...다..