A zeolitic material (Z-Y2) was synthesized from Coal Fly Ash (CFA) using a fusion/hydrothermal method under low-alkali condition (NaOH/CFA = 0.6). The adsorption performance of the prepared zeolite was evaluated by monitoring its removal efficiencies for Sr and Cs ions, which are well-known as significant radionuclides in liquid radioactive waste. The XRD (X-ray diffraction) patterns of the synthesized Z-Y2 indicated that a Na-A type zeolite was formed from raw coal fly ash. The SEM (scanning electron microscope) images also showed that a cubic crystal structure of size 1~3㎼ was formed on its surface. In the adsorption kinetic analysis, the adsorption of Sr and Cs ions on Z-Y2 fitted the pseudo-second-order kinetic model well, instead of the pseudo-first-order kinetic model. The second-order kinetic rate constant (k2) was determined to be 0.0614 g/mmol·min for Sr and 1.8172 g/mmol·min for Cs. The adsorption equilibria of Sr and Cs ions on Z-Y2 were fitted successfully by Langmuir model. The maximum adsorption capacity (qm) of Sr and Cs was calculated as 1.6846 mmol/g and 1.2055 mmol/g, respectively. The maximum desorption capacity (qdm) of the Na ions estimated via the Langmuir desorption model was 2.4196 mmol/g for Sr and 2.1870 mmol/g for Cs. The molar ratio of the desorption/adsorption capacity (qdm/qm) was determined to be 1.44 for Na/Sr and 1.81 for Na/Cs, indicating that the amounts of desorbed Na ions and adsorbed Sr and Cs ions did not yield an equimolar ratio when using Z-Y2.

LDHs(layered double hydroxides) are of use adsorbent to remove heavy metals, micro-organic pollutants as well as high concentration of phosphorus from wastewater to low concentration of surface water without pH adjustments. This study examined the generation condition of LDHs saturated with phosphorus. Less than 20% regeneration rate was obtained in the absence of alkali and regeneration solution. After the desorption of LDHs with several conditions of acid and alkali solution, more than 60% of regeneration rate could be expected in the case of using MgCl2 as regeneration solution.