This study was conducted to effectively supplement vitamin D and increase the consumption of ear mushroom based on the investigation of the quality characteristics of cookies containing ear mushroom supplemented with vitamin D. Cookies were made of 0%, 1%, 3%, and 5% ear mushroom powder treated by ultraviolet B. Increased addition of ear mushroom powder led to a decrease in the bulk density of the dough as well as a spread factor, color value, and hardness of the cookies. There was no significant difference in the loss rate, but the water content of the dough and cookies was increased. The total polyphenol content of cookies added with 1~5% ear mushroom powder was higher than that of the 0%. The DPPH free radical scavenging activity of cookies added with 5% ear mushroom powder (23.8%) was 2 times higher than that of the 0% (10.9%). The vitamin D2 content of cookies added with 5% ear mushroom powder (835.5 μg/100 g D.W.) was 44 times higher than that of the 0% (19.0 μg/100 g D.W.). Consequently, ear mushroom powder is considered to be suitable for the production of functional cookies because of high values of antioxidant activity and vitamin D2 content.

Nb-Si-B alloys with Nb-rich compositions are fabricated by spark plasma sintering for high-temperature structural applications. Three compositions are selected: 75 at% Nb (Nb0.7), 82 at% Nb (Nb1.5), and 88 at% Nb (Nb3), the atomic ratio of Si to B being 2. The microstructures of the prepared alloys are composed of Nb and T2 phases. The T2 phase is an intermetallic compound with a stoichiometry of Nb5Si3-xBx (0 ≤ x ≤ 2). In some previous studies, Nb-Si- B alloys have been prepared by spark plasma sintering (SPS) using Nb and T2 powders (SPS 1). In the present work, the same alloys are prepared by the SPS process (SPS 2) using Nb powders and hypereutectic alloy powders with composition 67at%Nb-22at%Si-11at%B (Nb67). The Nb67 alloy powders comprise T2 and eutectic (T2 + Nb) phases. The microstructures and hardness of the samples prepared in the present work have been compared with those previously reported; the samples prepared in this study exhibit finer and more uniform microstructures and higher hardness.

We investigate the microstructural and magnetic property changes of DyH2, Cu + DyH2, and Al + DyH2 diffusion-treated NdFeB sintered magnets with the post annealing (PA) temperature. The coercivity of all the diffusiontreated magnets increases with increasing heat treatment temperature except at 910oC, where it decreases slightly. Moreover, at 880oC, the coercivity increases by 3.8 kOe in Cu and 4.7 kOe in Al-mixed DyH2-coated magnets, whereas this increase is relatively low (3.0 kOe) in the magnet coated with only DyH2. Both Cu and Al have an almost similar effect on the coercivity improvement, particularly over the heat treatment temperature range of 790-880oC. The diffusivity and diffusion depth of Dy increases in those magnets that are treated with Cu or Al-mixed DyH2, mainly because of the comparatively easy diffusion path provided by Cu and Al owing to their solubility in the Nd-rich grain boundary phase. The formation of a highly anisotropic (Nd, Dy)2Fe14B phase layer, which acts as the shell in the core-shell-type structure so as to prevent the reverse domain movement, is the cause of enhanced coercivity of diffusion-treated Nd-Fe-B magnets.

A Ni-Ti-B alloy powder prepared by mechanical alloying (MA) of individual Ni, Ti, and B components is examined with the aim of elucidating the phase transitions and crystallization during heat treatment. Ti and B atoms penetrating into the Ni lattice result in a Ni (Ti, B) solid solution and an amorphous phase. Differential thermal analysis (DTA) reveals peaks related to the decomposition of the metastable Ni (Ti, B) solid solution and the separation of equilibrium Ni3Ti, TiB2, and τ-Ni20Ti3B6 phases. The exothermal effects in the DTA curves move to lower temperatures with increasing milling time. The formation of a TiB2 phase by annealing indicates that the mechanochemical reaction of the Ni-Ti-B alloy does not comply with the alloy composition in the ternary phase diagram, and Ti-B bonds are found to be more preferable than Ni-B bonds.

The crystallization effects of boron (B) powder on the phase, full width at half maximum (FWHM) values, and critical properties were investigated for in-situ reacted MgB2 bulk superconductors. The semi-crystalline B powder was heat-treated at different temperatures of 1000, 1300 and 1500˚C for 5 hours in an Ar atmosphere. Then, using as-received and heat-treated B powders, the MgB2 samples were prepared at 600˚C for 40 hours in an Ar atmosphere. As the heat-treatment temperature of the B powder increased, both the particle size of the B powder and crystalline phase increased. In the case of MgB2 samples using B powders heat-treated at above 1300˚C, unreacted magnesium (Mg) and B remained due to the improved crystallinity of the B powder. As the heat-treatment temperature of B powder increased, the critical current density of MgB2 decreased continuously due to the reduction of grain boundary density and superconducting volume caused by unreacted Mg and B.

2012년 2월부터 11월까지 인천 지역에서 유통된 건고추 및 고춧가루 193건을 대상으로 아플라톡신 B1과 오크라톡 신 A의 오염도를 조사하였다. Immunoaffinity column 및 HPLC를 이용한 시험법은 모두 80% 이상의 회수율을 보였고, 아플라톡신 B1 및 오크라톡신 A의 검출한계는 각각 0.13 μg/kg, 0.30 μg/kg였다. 오염도 조사를 한 결과 아플라 톡신 B1은 17.1%의 검출율을 보였고 오크라톡신 A는 20.7% 의 검출율을 보였으며, 아플라톡신 B1의 검출농도는 0.14~ 9.67 μg/kg였고, 오크라톡신 A의 검출 농도는 0.31~3.31 μg/ kg였다. 이는 우리나라 식품공전 상의 기준인 10 μg/kg(아 플라톡신 B1), 7 μg/kg(오크라톡신 A)보다는 낮은 수치로 비교적 안전한 수준이었다.

High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundary. The maximum thickness of the Dy shell was approximately 70 nm. The maximum coercivity of the Dy sputter coated samples(sintered samples) increased from 1162.42 to 2020.70 kA/m. The microstructures of the (Nd,Dy)2Fe14B phases were effectively controlled, resulting in mproved magnetic properties. The increase in coercivity of the Nd-Fe-B sintered magnet is discussed from a micro- structural point of view.

In the present work, 6061 Al-B4C sintered composites containing different B4C contents were fabricated and their characteristic were investigated as a function of sintering temperature. For this, composite powders and their compacts with B4C various contents from 0 to 40 wt.% were fabricated using a planetary ball milling equipment and cold isostatic pressing, respectively, and then they were sintered in the temperature ranges of 580 to 660o C. Above sin- tering temperature of 640o C, real density was decreased due to the occurrence of sweat phenomena. In addition, it was realized that sinterability of 6061Al-B4C composite material was lowered with increasing B4C content, resulting in the decrease in its real density and at the same time in the increment of porosity.

In this study, GaN powders were synthesized from gallium oxide-hydroxide (GaOOH) through an ammonification process in an NH3 flow with the variation of B2O3 additives within a temperature range of 300-1050˚C. The additive effect of B2O3 on the hexagonal phase GaN powder synthesis route was examined by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and Fourier transformation infrared transmission (FTIR) spectroscopy. With increasing the mol% of B2O3 additive in the GaOOH precursor powder, the transition temperature and the activation energy for GaN powder formation increased while the GaN synthesis limit-time (tc) shortened. The XPS results showed that Boron compounds of B2O3 and BN coexisted in the synthesized GaN powders. From the FTIR spectra, we were able to confirm that the GaN powder consisted of an amorphous or cubic phase B2O3 due to bond formation between B and O and the amorphous phase BN due to B-N bonds. The GaN powder synthesized from GaOOH and B2O3 mixed powder by an ammonification route through β-Ga2O3 intermediate state. During the ammonification process, boron compounds of B2O3 and BN coated β-Ga2O3 and GaN particles limited further nitridation processes.

Effect of Cu and powder mixing with Cu-free (Nd, Dy)-Fe-B jet-milled powder on the magnetic properties of sintered magnets was investigated. The coercivity of a magnet prepared from the Cu-free (Nd, Dy)-Fe-B powder was about 10 kOe even though the alloy powder already contained some Dy (3.5 wt%). When small copper powder was blended, however, the coercivity of the magnet increased almost 100%, exhibiting about 20 kOe. On the contrary, the coercivity enhancement was moderate, about 4 kOe, when dysprosium content in the sintered magnet was simply increased to 4.9 wt% by the addition of small 3 powder.

In this study, the effect of milling time on the microstructure and phase transformation behaviors of Ni-12 wt.%B powders was investigated using vibratory ball milling process. X-ray diffraction patterns showed that the phase transformation of mixed Ni-B elemental powder occurred after 50 hours of milling, with a formation of nickel boride phases. Through the study of microstructures in mechanical alloying process, it was considered that ball milling strongly accelerates solid-state diffusions of the Ni and B atoms during mechanical alloying process. The results of X-ray photoelectron spectroscopy showed that most of B atoms in the powder were linked to Ni with a formation of nickel boride phases after 200 hours of milling. It was finally concluded that mechanical alloying using ball milling process is feasible to synthesize fine and uniform nickel boride powders.

In this study, the sintering behavior of (Nd, Dy)-Fe-B powder which fabricated by strip-casting was investigated with various sintering temperatures and holding times. The relative density over 99% could be obtained by both sintering at for 1h and sintering at for 20h. The grain growth was observed in sintered specimen at compared to one at . The isothermal sintering process below led to suppress grain growth showing the improved magnetic properties. The phase transformation of Nd-rich was confirmed by X-ray diffraction pattern.

The electromagnetic wave absorption sheets were fabricated by mixing of nanocrystalline soft magnetic powder, charcoal powder and polymer based binder. The complex permittivity, complex permeability, and scattering parameter have been measured using a network analyzer in the frequency range of 10 MHz10 GHz. The results showed that complex permittivity of sheets was largely dependent on the frequency and the amount of charcoal powder : The permittivity was improved up to 100 MHz, however the value was decreased above 1 GHz. The power loss of electromagnetic wave absorption data showed almost the same tendency as the results of complex permittivity. However, the complex permeability was not largely affected by the frequency, and the values were decreased with the addition of charcoal powder. Based on the results, it can be summarized that the addition of charcoal powder was very effective to improve the EM wave absorption in the frequency range of 10 MHz1 GHz.

Carbon was known to be one of effective additives which can improve the flux pinning of at high magnetic fields. In this study, glycerin was selected as a chemical carbon source for the improvement of critical current density of . In order to replace some of boron atoms by carbon atoms, the boron powder was heat-treated with liquid glycerin. The glycerin-treated boron powder was mixed with an appropriate amount of magnesium powder to composition and the powder pallets were heat treated at for 30 min in a flowing argon gas. It was found that the superconducting transition temperature of prepared using glycerin-treated boron powder was 36.6 K, which is slightly smaller than (37.1 K) of undoped . The critical current density of was higher than that of undoped and the improvement effect was more remarkable at higher magnetic fields. The , decrease and increase associated with the glycerin treatment for boron powder was explained in terms of the carbon substitution to boron site.

자체연소반응법에 의하여 탄화붕소(B4C)를 합성함에 있어서 자체적으로는 반응이 이루어지지 않아서 간접점화법인 화학로법(Chemical Furnace)으로 합성을 하였으며, 성형압력과 몰비를 변수로 하여 연소온도 및 연소속도의 변화를 측정하였다. 성형밀도가 이론밀도의 70%에서 연소온도와 연소속도가 가장 높았으며, 몰비에 대한 영향은 표준비였을 때 연소온도와 연소속도가 가장 높았다. 그리고 성형밀도에 따른 입자의 크기변화는 성형밀도가 높을수록 입자의 크기는 작아졌으며 따라서 비표면적은 커졌다.