Al2O3 has excellent sintering properties and is important in semiconductor manufacturing processes that require high-temperature resistance and chemical inertness in a plasma environment. In this study, a comprehensive analysis of the chemical characteristics, physical properties, crystal structure, and dispersion stability of three commercially available Al2O3 powders was conducted. The aim was to provide a technological foundation for selecting and utilizing appropriate Al2O3 powders in practical applications. All powders exhibited α-Al2O3 as the main phase, with the presence of beta-phase Na2O-11Al2O3 as the secondary phase. The highest Na+ ion leaching was observed in the aqueous slurry state due to the presence of the secondary phase. Although the average particle size difference among the three powders was not significant, distinct differences in particle size distribution were observed. ALG-1SH showed a broad particle size distribution, P162 exhibited a bimodal distribution, and AES-11 displayed a uniform unimodal distribution. Highconcentration Al2O3 slurries showed differences in viscosity due to ion release when no dispersant was added, affecting the electrical double-layer thickness. Polycarboxylate was found to effectively enhance the dispersion stability of all three powders. In the dispersion stability analysis, ALG-1SH exhibited the slowest sedimentation tendency, as evidenced by the low TSI value, while P162 showed faster precipitation, influenced by the particle size distribution.

Al2O3 nanosol dispersed under ethanol or N-Methyl-2-pyrrolidone(NMP) was studied and optimized with various dispersion factors and by utilizing the silane modification method. The two kinds of Al2O3 powders used were prepared by thermal decomposition method from aluminum ammonium sulfate(AlNH4(SO4)2) while controlling the calcination temperature. Al2O3 sol was prepared under ethanol solvent by using a batch-type bead mill. The dispersion properties of the Al2O3 sol have a close relationship to the dispersion factors such as the pH, the amount of acid additive(nitric acid, acetic acid), the milling time, and the size and combination of zirconia beads. Especially, Al2O3 sol added 4 wt% acetic acid was found to maintain the dispersion stability while its solid concentration increased to 15 wt%, this stability maintenance was the result of the electrostatic and steric repulsion of acetic acid molecules adsorbed on the surface of the Al2O3 particles. In order to observe the dispersion property of Al2O3 sol under NMP solvent, Al2O3 sol dispersed under ethanol solvent was modified and solventexchanged with N-Phenyl-(3-aminopropyl)trimethoxy silane(APTMS) through a binary solvent system. Characterization of the Al2O3 powder and the nanosol was observed by XRD, SEM, ICP, FT-IR, TGA, Particles size analysis, etc.

NiO catalysts/Al2O3/FeCrAl alloy foam for hydrogen production was prepared using atomic layer deposition (ALD)and subsequent dip-coating methods. FeCrAl alloy foam and Al2O3 inter-layer were used as catalyst supports. To improve thedispersion and stability of NiO catalysts, an Al2O3 inter-layer was introduced and their thickness was systematically controlledto 0, 20, 50 and 80nm using an ALD technique. The structural, chemical bonding and morphological properties (includingdispersion) of the NiO catalysts/Al2O3/FeCrAl alloy foam were characterized by X-ray diffraction, X-ray photoelectronspectroscopy, field-emission scanning electron microscopy and scanning electron microscopy-energy dispersive spectroscopy. Inparticular, to evaluate the stability of the NiO catalysts grown on Al2O3/FeCrAl alloy foam, chronoamperometry tests wereperformed and then the ingredient amounts of electrolytes were analyzed via inductively coupled plasma spectrometer. We foundthat the introduction of Al2O3 inter-layer improved the dispersion and stability of the NiO catalysts on the supports. Thus, whenan Al2O3 inter-layer with a 80nm thickness was grown between the FeCrAl alloy foam and the NiO catalysts, it indicatedimproved dispersion and stability of the NiO catalysts compared to the other samples. The performance improvement can beexplained by optimum thickness of Al2O3 inter-layer resulting from the role of a passivation layer.