In this work, we prepared a heterojunction anode with a surface layer of SnO2-Sb-Ni (SSN) on a Ti/IrO2 electrode by thermal decomposition to improve the electrochemical activity of the Ti/IrO2 electrode. The Ti/IrO2-SSN electrode showed significantly improved electrochemical activity compared with Ti/IrO2. For the 0.1 M NaCl and 0.1 M Na2SO4 electrolytes, the onset potential of the Ti/IrO2-SSN electrode shifted in the positive direction by 0.1 VSCE and 0.4 VSCE, respectively. In 2.0-2.5 V voltages, the concentration in Ti/IrO2-SSN was 2.59-214.6 mg/L Cl2, and Ti/IrO2 was 0.55-49.21 mg/L Cl2. Moreover, the generation of the reactive chlorine species and degradation of Eosin-Y increased by 3.79-7.60 times and 1.06-2.15 times compared with that of Ti/IrO2. Among these voltages, the generation of the reactive chlorine species and degradation of Eosin-Y were the most improved at 2.25 V. Accordingly, in the Ti/IrO2-SSN electrode, it can be assumed that the competitive reaction between chlorine ion oxidation and water oxidation is minimized at an applied voltage of 2.25V.

This study is based on the electrochemical theory which aims to get the quantitative evaluation about corrosion protection of Zn-Sn metal spray method. The various existing corrosion resistance method and various mixture ratio of Zn-Sn metal spray method is applied with structural steel which is measured change of polarization resistance and corrosion potential. So corrosion protection of Zn-Sn metal spray method is tested. Consequently, coating side of Zn-Sn metal spray method was lower than electric potential of a structural steel adhesion side. So, Galvanic Protection of Zn-Sn metal spray found that structural steel advanced system. Accordingly, Zn-Sn metal spray method is expected as corrosion protection technology excellent in corrosion prevention of structural steel.

In this study, corrosion potential (Ecorr), corrosion rate, and polarization resistance were measured aimed at inorganic inhibitors (passive film type) and organic inhibitors (absorption type). The experiment was conducted using potentiostat for the variable molar ratio and chloride ion concentration of the components of inhibitors in an aqueous solution of saturated calcium hydroxide targeting corrosion. As a result, it was possible to ensure an anticorrosive performance of at least a 1.2 molar ratio of inorganic inhibitors. Also, the organic inhibitors ensured the prevention of the anticorrosive performance of at least about a 0.3 molar ratio. It also showed the tendency that between polarization resistance and corrosion rate, Ecorr and corrosion rate is inversely proportional to the linear. Conversely, the tendency between polarization resistance and Ecorr is proportional to the linear. Also, a distinct difference in organic and inorganic inhibitors’ relationship to Ecorr, corrosion rate, and polarization resistance was not shown.

In this study, in order to comprehend performance of corrosion inhibitor, the experiment study was conducted about corrosion characteristic of 3 steps(0.0, norm 1/2, norm) compared to organic corrosion inhibitor standard use of liquid and molar 3 steps(0.0, 0.3, 0.6%) of Chloride by added amount of inorganic corrosion inhibitor by the corrosion inhibitor types about 2.4kg/m3, 4.8kg/m3 based on Chloride ion content 1.2kg/m3 for service life prediction of concrete structure by using Poteniostat.