In order to investigate the effect of irradiation by 60Co-γrays as well as the e thermal treatment on the dielectric deterioration in ethylene propylene rubber, insulating material for electric cables used in atomic power plants, charging discharging current, residual built- up voltage and dielectric properties are measu discussed in this study. Variance in the characteristic of relative dielectric constant as a function of tem was observed in relatively high dose of irradiation. Since glass transition tem appeared at tens of degree Celsius below zero, the characteristic is attributed orientation polarization. Dielectric loss is generally increased, with increasing d irradiation in the characteristic of dielectric loss as a function of temperature, No d loss by thermal treatment was observed. Dielectric resistance decreases with increa of irradiation in the characteristic of charging current as a function of temperature be considered that dielectric resistance seems to be recovered by thermal treatm characteristic of discharging current as a function of time in the specimen less ir become similar to that of the unirradiated, when thermal treated. A peak is shown residual built- up voltage as a function of time, and the corresponding time of the shorten as increasing dose of irradiation. It is also observed that the corresponding the peak is lengthened by thermal treatment.

Pure and fine, two-component titanate powders (barium titanate, calcium titanate etc.) were synthesized by an ethylene glycol method. Titanium isopropoxide and other metal ionic salts were dissolved in liquid-type ethylene glycol without any precipitation. In non-aqueous system, the amount of ethylene glycol affected the solubility and homogeneity of metal cation sources in the solution. At the optimum amount of the polymer, the metal ions were dispersed effectively in solution and a homogeneous polymeric network was formed. Most of the synthesized powders had sub-micron or nano-size primary particles after calcination and the agglomerated calcined powders were easily ground by ball milling process. All synthesized titanate powders had stable crystallization behavior at low temperature and high specific surface area after ball milling. The crystallization behavior and the microstructures of the calcined powders were affected on the ethylene glycol content.

The charge and discharge current in EPR(Ethylene Propylene Rubber), which were irradiated with the radiant capacity of 0~600 ［kgy/h］, have been measured in order to investigate the influence of the atmosphere (oxygen, air and vacuum) on electrical properties. It has been shown that the charge and discharge current increase as the amount of radiant capacity increases in air and vacuum atmosphere. This electrical property degradation can be speculated due to that the C＝O radicals or impurities, which comes from during shaping process, may act as dipoles. On the other hand, the charge and discharge current are shown to be higher in the amount of 1［kgy/h］ than these in 10［kgy/h］ in air atmosphere, because the charge and discharge current can be increased as the exposure time is extended with slower rate. Under the same amount of irradiation, the charge and discharge current in oxygen atmosphere are shown to be higher than those in vacuum. This is possibly due to that the main chain can be broken by oxidation when it is exposed to the γ -rays.

The present experirnents on cryopreservation were carried out to investigate effect of solution toxicity, equilibration time and cell stages on the post-thaw survival of mouse morulae and blastocyst embryos cryopreserved by vitrification in EFS solution. The mouse embryos were exposed to the EFS solution in one step at room temperature, kept in the EFS solution during different period for toxicity test, vitrified in liquid nitrogen and thawed rapidly. After the mouse morulae embryos were exposed to EFS solution for 2 and 5 ruin. at room temperature and then they were washed in 0.5 M sucrose solution and basal mediurn(D-PBS + 10% FCS), they were cultured to examined cryoprotectant toxicity induced injury during exposure, most of embryos developed to expanded blastocysts(100 and 90.0%). However, when the exposure time was extended to 10 and 20 min, these development rates dropped dramatically in 10 ruin. (75.0%) and 20 ruin. (4.5%), respectively. When the compacted morulae were vitrified in EFS solution after equilibration for 2 and 5 min, the embryos have developed to normal blastocyst following thawing, washing and culture processes was 89.3 and 89.6%. However, when the exposure time was expanded to 10 ruin, this survival rate dropped to 68.8%. When the blastocyst were vitrified in EFS solution after equilibration for 2, 5 and 10 minutes, the survival rate of embryos which developed to normal blastocyst following thawing and culture processing were 58.5, 46.7 and 22.4%, respectively. The optimal time of equilibration of mouse morula and blastocysts in EFS solution seemed o be 2 and 5 ruin.

The post-thaw survival of mouse embryos of the various developmental stages was determined after cryopreservation by vitrification in a solution containing ethylene glycol, Ficoll and sucrose (EFS). All the embryos were equilibrated for 2 minutes just prior to freezing. The number of blastomeres during in vitro development was counted by nuclei higher rates of post-thaw survival were obtained from the embryos of 2-cell(92.2%), 8-cell(77.2%) or morula stage(90.0%) than those of blastocyst stage(62.7%). The number of blastomeres per embryo following in vitro culture for 24 hours was significantly(P<0.05) smaller as 66.0f22.3 in vitrified and thawed morulae than fresh morulae(91.712.2).

Transesterification reaction between dimethyl phthalate and ethylene glycol was kinetically investigated in the presense of various metal nitrate catalysts at 170℃. The reaction rates measured by the amount of distilled methanol from the reaction vessel. The transesterification reaction was carried out under the first order conditions respect to the concentration of dimethyl phthalate and catalyst, respectively. The over all order was 2nd. By Arrhenius plot, the activation energy was calculated as 17.4kcal/mole and 17.2kcal/mole on the transesterification reaction with zinc nitrate and lead nitrate, respectively. Apparent rate constant, k' was appeared linear about concentration of catalyst.

시차주사 열분석기를 이용하여 poly(ethylene oxide)(PEO)/poty(styrene-co-acrylic acid) (SAA) blonds에 대한 등온 결정화 속도를 blend의 조성, 사용한 SAA의 공중합조성 및 결정화 온도에 따라 조사하였다. 실험결과는 Avrami 방정식을 이용하여 분석하였다. Avrami지수는 결정화 온도에 관계없이 거의 모든 blend 시료에서 2의 값을 나타내었다. 결정화 속도는 blend시료의 SAA 함량 및 사용한 SAA 공중합체의 아크릴산함량이 증가함에 따라 급격히 느려졌다.