An optimum route to fabricate oxide dispersion strengthened ferritic superalloy with desired microstructure was investigated. Two methods of high energy ball milling or polymeric additive solution route for developing a uniform dispersion of Y2O3 particles in Fe-Cr-Al-Ti alloy powders were compared on the basis of the resulting microstructures. Microstructural observation revealed that the crystalline size of Fe decreased with increases in milling time, to values of about 15-20 nm, and that an FeCr alloy phase was formed. SEM and TEM analyses of the alloy powders fabricated by solution route using yttrium nitrate and polyvinyl alcohol showed that the nano-sized Y-oxide particles were well distributed in the Fe based alloy powders. The prepared powders were sintered at 1000 and 1100 oC for 30 min in vacuum. The sintered specimen with heat treatment before spark plasma sintering at 1100 oC showed a more homogeneous microstructure. In the case of sintering at 1100 oC, the alloys exhibited densified microstructure and the formation of large reaction phases due to oxidation of Al.

Fe-base superalloy powders with Y2O3 dispersion were prepared by high energy ball milling, followed by sparkplasma sintering for consolidation. High-purity elemental powders with different Fe powder sizes of 24 and 50mm were usedfor the preparation of Fe-20Cr-4.5Al-0.5Ti-O.5Y2O3 powder mixtures (wt%). The milling process of the powders was carriedout in a horizontal rotary ball mill using a stainless steel vial and balls. The milling times of 1 to 5 h by constant operation(350 rpm, ball-to-powder ratio of 30:1 in weight) or cycle operation (1300 rpm for 4 min and 900 rpm for 1 min, 15:1) wereapplied. Microstructural observation revealed that the crystalline size of Fe decreased with an increase in milling time by cyclicoperation and was about 15nm after 3 h, forming a FeCr alloy phase. The cyclic operation had an advantage over constantmilling in that a smaller-agglomerated structure was obtained. The milled powders were sintered at 1100oC for 30 min invacuum. With an increase in milling time, the sintered specimen showed a more homogeneous microstructure. In addition, ahomogenous distribution of Y-compound particles in the grain boundary was confirmed by EDX analysis.