In this study, a new type of composite material combined with carbonyl iron, a relatively strong ferromagnetic material, was prepared to overcome the current application limitations of Prussian blue, which is effective in removing radioactive cesium. The surface of the prepared composite was analyzed using SEM and XRD, and it was confirmed that nano-sized Prussian Blue was synthesized on the particle surface. In order to evaluate the cesium removal ability, 0.2 g of the composite prepared for raw cesium aquatic solution at a concentration of 5 μg was added and reacted, resulting in a cesium removal rate of 99.5 %. The complex follows Langmuir’s adsorption model and has a maximum adsorption amount (qe) of 79.3 mg/g. The Central Composite Design (CCD) of the Response Surface Method (RSM) was used to derive the optimal application conditions of the prepared composite. The optimal application conditions achieved using Response optimization appeared at a stirring speed of pH 7, 17.6 RPM. The composite manufactured through this research is a material that overcomes the Prussian Blue limit in powder form and is considered to be excellent economically and environmentally when applied to a cesium removal site.

Fabrication of a ferromagnetic composite powder for the magnesium and BaFe12O19 system by mechanical alloying (MA) is investigated at room temperature. Mixtures of Mg and BaFe12O19 powders with a weight ratio of Mg:BaFe12O19 = 4:1, 3:2, 2:3 and 1:4 are used. Optimal MA conditions to obtain a ferromagnetic composite with fine microstructure are investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that Mg-BaFe12O19 composite powders in which BaFe12O19 is dispersed in Mg matrix are successfully produced by MA of BaFe12O19 with Mg for 80 min. for all compositions. Magnetization of Mg- BaFe12O19 composite powders gradually increases with increasing the amounts of BaFe12O19, whereas coercive force of MA powders gradually decreases due to the refinement of BaFe12O19 powders with MA time for all compositions. However, it can be seen that the coercivity of Mg-BaFe12O19 MA composite powders with a weight ratio of Mg:BaFe12O19=4:1 and 3:2 for MA 80 min. are still high, with values of 1260 Oe and 1320 Oe compared to that of Mg:BaFe12O19=1:4. This clearly suggests that the refinement of BaFe12O19 powders during MA process for Mg:BaFe12O19=4:1 and 3:2 tends to be suppressed due to ductile Mg powders.

Most structures require high reliability to ensure safety and soundness. The materials used for these structures are not only defective in the manufacturing process and construction process, but also cause generation and progress of defects due to operation of various complex use environments. In order to improve the reliability of the structure, it is very important to detect and estimate the defect size. The method of evaluating these defects without damaging the structure is a non-destructive method. In this paper, an aluminum probe of AC potential drop(ACPD) method is applied to the evaluation of two-dimensional artificial defects in ferromagnetic materials. Since the potential drop of the defect end is larger than that of the sound area, the defect can be detected and its position can be clearly confirmed, and the potential drops are changed according to the depth of the defect. The potential drop ratio (Vjmax/Vs) of the defective area has a large value for the defect. The relationship between the potential drop ratio (Vjmax/Vs) of 10 kHz and the defect depth can reduce the error in predicting the depth.

In this study, we investigated the effect of annealing conditions on the ferromagnetic resonance(FMR) of yttrium iron garnet (Y3Fe5O12, YIG) thin film prepared on gadolinium gallium garnet (Gd3Ga5O12, GGG) substrate. The YIG thin films were grown by rf magnetron sputtering at room temperature and were annealed at various temperatures from 700 to 1000 ˚C. FMR characteristics of the YIG thin films were investigated with a coplanar waveguide FMR measurement system in a frequency range from 5 to 20 GHz. X-ray diffraction(XRD) and X-ray photoelectron spectroscopy(XPS) were used to characterize the phase formation, crystal structure and composition of the YIG thin films. Field dependent magnetization curves at room temperature were obtained by using a vibrating sample magnetometer(VSM). The FMR measurements revealed that the resonance magnetic field was highly dependent on the annealing condition: the lowest FMR linewidth can be observed for the 800 ˚C annealed sample, which agrees with the VSM results. We also found that the Fe and O composition changes during the annealing process play important roles in the observed magnetic properties.

This paper studies the repulsion occurring between the permanent magnet by the simulation analysis. Nowadays, there are many cases such as magnetic levitation, safety bumper device and so on using the properties of the permanent magnet. As the neodymium magnet of the powerful ferromagnetic material is less expensive by comparing with the strong magnetic force for industrial, medical areas and etc., it can be used at the various applications. The prediction of the magnetic force is becoming increasingly important in order to be used effectively permanent magnet in various fields. Therefore, the results of the magnetostatics by Ansys and the MAXWELL of commercial electromagnetic analysis software are analyzed and compared. Magnetic force is inversely proportional to the distance and power. In this paper, the permanent magnet was simulated and compared by the two permanent magnets of the small sizes with the diameter of 4mm and the length of 8mm. In addition, the forces between the ferromagnetic iron and permanent magnets are simulated.

목 적 : 3.0T 자기 공명 영상에서 강자성 임플란트로 인해 발생한 자화감수성 인공음영에 대한 시퀀스별 WARP기법의 적정한 VAT(view angle tilting)값을 알아보았다. 대상 및 방법 : 자화감수성 인공음영(susceptibility artifact image)이 head용 워터 팬텀영상의 왜곡정도를 평가하기 위하여 head용 워터 팬텀에 강자성 임플란트(ferromagnetic implant)인 금속 와이어를 부착하여 영상을 획득하였다. 진행하였고(VAT(view angle tilting)) Warp를 사용하였다. 사용된 장비는 3.0T MRI system(MAGNETOM Skyra, Siemens, Munich, Germany)이었으며 20ch head/neck coil을 사용하여 TSE T2, TSE T1, FLAIR, Turbo IR T1 시퀀스에 WARP를 적용하여 VAT를 0~100% 범위내에서 10%씩 변화하여 각각 24개의 axial 영상을 얻었다. TSE T2 영상변수는 TR/TE 4410ms/79ms, Matrix 512×291이었으며, TSE T1 영상변수는 TR/TE 693ms/10ms, Matrix 512×291이었으며, Turbo IR T1 영상변수는 TR/TE 2000ms/9.5ms, Matrix 384×307이었으며, FLAIR 영상변수는 TR/TE 9000ms/96ms, Matrix 384×180이었다. 시퀀스별로 slice thickness 4mm, slice gap 0.4mm, NEX 1, bandwidth는 500Hz 였다. 정량평가는 팬텀영상의 대부분을 ROI로 설정 하여 표준편차를 구하였다. 정성 평가는 팬텀 영상 내에 dark area크기, image blurring 정도를 5점 척도로 하여 영상의 변화가 없는 경우 1점, 영상의 질이 약간 우수한 경우 2점, 보통 3점, 우수한 경우 4점, 매우 우수한 경우 5점으로 숙련된 방사선사 3명이 관찰 후 평가하였다. 결 과 : 정량분석으로 TSE T2와 TSE T1의 표준편차(SD)는 VAT 10%에서 VAT 적용전보다 많은 감소를 보였으며, VAT가 증가 할수록 감소하는 경향을 나타냈다. 그러나 IR 계열의 FLAIR와 Turbo IR T1은 WARP의 적용에 따른 영상차이가 없었다. 변동계수는 모든 시퀀스에서 30%이하였다. 또한 VAT 변화에 따라 영상의 위치변화도 나타났다. 정성분석으로 TSE T2는 VAT가 30~60%일 때 우수한 것으로 나타났고, TSE T1은 VAT가 10~70%일 때 우수한 것으로 나타났다. FLAIR와 Turbo IR T1은 WARP사용에 따른 영상의 변화가 없었다 결 론 : WARP는 TSE T2와 TSE T1의 자화감수성 인공음영을 줄이는데는 매우 효과적인 영상기법이었다. 그러나 WARP는 VAT를 증가시키면 image blurring도 증가함으로 VAT값을 최소화해서 사용 되어져야 할 것으로 사료된다.

강자성 판의 자기-열-탄성 상호작용을 고찰하기 위하여 자기-열-탄성에 관한 일반화된 변분원리에 기초한 이론적인 모델이 제안되었다. 자탄성 선형화이론과 섭동법을 사용하여, 온도장과 자기장으로 재하된 단순지지 강자성 평판의자-탄성 좌굴과 자기-열-탄성 좌굴거동을 해석하였다. 또한 해석적인 고찰이 어려운 보다 복잡한 강자성 판의 자기-열-탄성 거동을 모사하기 위하여 비선형 유한요소 모형을 개발하였다. 이 유한요소모형을 이용하여 유한한 강자성 판의 자기-열-탄성 과 좌굴거동 그리고, 이에대한 온도장과 자기장의 영향에 대하여 고찰하였다.

순도가 자기적 임계현상에 어떠한 영향을 주는가를 보기 위해 여러 순도의 니켈에서 비저항의 온도의존성을 관찰하였다. 비저항은 Lock-In 증폭기를 사용하여 교류저항측정법으로 측정하였으며 시료를 솔레노이드식으로 감아 저항부분과 인덕터부분의 신호를 함께 관찰할 수 있도록 하였다. 큐리온도는 이들 신호들이 갑작스럽게 변하는 온도로 결정하여UT으며 저항부분과 인덕터부분의 신호에서 결정한 큐리온도값들은 서로 잘 일치함을 볼 수 있었다. 비저항의 온도에 따른 일차미분에서 비열의 임계지수를 결정하였으며 큐리온도와 마찬가지로 임계지수의 순도의존성은 실험오차내에서는 없음이 관찰되었다.

본 연구는 총 15명의 정상인 지원자를 대상으로 1.5T와 3.0T의 자기공명영상기기(Philips, Medical System, Achieva)를 이용하여 강자성 인공물을 최소화하기 위한 최적의 Tesla를 알아보고자 하였다. 평가는 신호대잡음비 평가, 강자성 인공물이 형성된 부위의 길이와 Histogram을 평가하였다. 분석방법으로는 T1, T2 sagitt al 영상의 Background의 4 부위에 관심영역을 설정하고 L3, L4, L5의 각 추체부에 관심영역을 설정한 후 신호대잡음비 값을 측정하였고, 인공물이 형성된 3 부위에 관심영역을 설정하고 길이 값을 측정하였고, Im age J 프로그램을 이용해 인공물 영역의 히스토그램 분포 값을 측정하였다. 본 실험에 대한 결과로 신호대잡음비 평가에서 L3에서는 1.5T와 3.0T 사이에 별 차이가 없는 것으로 나타났고, L4, L5에서는 큰 차이가 있는 것으로 나타났다(p<0.05). 강자성 인공물이 형성된 3 부위의 길이는 3.0T에 비해 1.5T가 더 짧아 주변 조직에 대한 진단적 정보를 더 얻을 수 있는 것으로 나타났다(p<0.05). Histogram평가에서는 3.0T보다 1.5T 가 Count값이 높게 나타났다(p<0.05). 결론적으로 1.5T와 3.0T의 신호대 잡음비, 강자성 인공물의 길이, Hist ogram을 비교 평가해 봤을 때, Spine MRI 검사 시에 PLIF 등 디스크 수술을 받은 환자에게는 Low Tesla로 검사가 최적의 영상정보를 얻을 수 있었다.