In this study, we investigated the change in fracture properties after friction stir welding on Al606. In the L-T direction test, the fracture toughness of the unwelded base material was 275 MPa, and the specimen subjected to friction stir welding (FSW) was 227 MPa, showing that the fracture toughness decreased significantly with friction stir welding. In the T-L direction test, the difference between the base material and the weld material was not large, but the fracture toughness was shown to decrease during welding. In the comparison of the L-T direction and the T-L direction, it was found that both the base material and the weld material showed high fracture toughness in the L-T direction.In this study, the following conclusions were obtained after friction stir welding of Al 6061-T6.

Power converter devices require a high level of quality because they have a high direct connection with vehicle operation. Therefore, structural bonding was carried out by friction stir welding with excellent mechanical properties. Friction stir welding can cause structural deflection depending on the load of the welding tool, so it is important to control this for high quality flatness. In this study, pre-welding was performed before welding to minimize deflection generated during welding. And deflection reduction data according to the location of pre-welding were analyzed through dynamic analysis. As a result, based on computerized data rather than experimental data an optimized position of pre-welding was secured to minimize the deflection that occurs during friction stir welding. Through this, a process guide that enables high quality structural bonding was presented.