Layered LiNi0.83Co0.11Mn0.06O2 cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, nondoping pristine LiNi0.83Co0.11Mn0.06O2 cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical α-NaFeO2-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dualdoped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).

Graphene is a single atomic layer of carbon atoms, and has exceptional electrical, mechanical, and optical characteristics. It has been broadly utilized in the fields of material science, physics, chemistry, device fabrication, information, and biology. In this review paper, we briefly investigate the ideas, structure, characteristics, and fabrication techniques for graphene applications in lithium ion batteries (LIBs). In LIBs, a constant three-dimensional (3D) conductive system can adequately enhance the transportation of electrons and ions of the electrode material. The use of 3D graphene and graphene-expansion electrode materials can significantly upgrade LIBs characteristics to give higher electric conductivity, greater capacity, and good stability. This review demonstrates several recent advances in graphenecontaining LIB electrode materials, and addresses probable trends into the future.

In this study, an experiment is performed to recover the Li in Li2CO3 phase from the cathode active material NMC (LiNiCoMnO2) in waste lithium ion batteries. Firstly, carbonation is performed to convert the LiNiO, LiCoO, and Li2MnO3 phases within the powder to Li2CO3 and NiO, CoO, and MnO. The carbonation for phase separation proceeds at a temperature range of 600oC~800oC in a CO2 gas (300 cc/min) atmosphere. At 600~700oC, Li2CO3 and NiO, CoO, and MnO are not completely separated, while Li and other metallic compounds remain. At 800 oC, we can confirm that LiNiO, LiCoO, and Li2MnO3 phases are separated into Li2CO3 and NiO, CoO, and MnO phases. After completing the phase separation, by using the solubility difference of Li2CO3 and NiO, CoO, and MnO, we set the ratio of solution (distilled water) to powder after carbonation as 30:1. Subsequently, water leaching is carried out. Then, the Li2CO3 within the solution melts and concentrates, while NiO, MnO, and CoO phases remain after filtering. Thus, Li2CO3 can be recovered.

Free-standing electrodes of CuO nanorods in carbon nanotubes (CNTs) are developed by synthesizing porous CuO nanorods throughout CNT webs. The electrochemical performance of the free-standing electrodes is evaluated for their use in flexible lithium ion batteries (LIBs). The electrodes comprising CuO@CNT nanocomposites (NCs) were characterized by charge-discharge testing, cyclic voltammetry, and impedance measurement. These structures are capable of accommodating a high number of lithium ions as well as increasing stability; thus, an increase of capacity in long-term cycling and a good rate capability is achieved. We demonstrate a simple process of fabricating free-standing electrodes of CuO@ CNT NCs that can be utilized in flexible LIBs with high performance in terms of capacity and cycling stability.

Using a high pressure homonizer, we report on the electrochemical performance of Li4Ti5O12(LTO) particles manufactured as anode active material for lithium ion battery. High-pressure synthesis processing is performed under conditions in which the mole fraction of Li/Ti is 0.9, the synthesis pressure is 2,000 bar and the numbers of passings-through are 5, 7 and 10. The observed X-ray diffraction patterns show that pure LTO is manufactured when the number of passings-through is 10. It is found from scanning electron microscopy analysis that the average size of synthesized particles decreases as the number of passings-through increases. LiCoO2-based active cathode materials are used to fabricate several coin half/full cells and their battery characteristics such as lifetime, rate capability and charge transfer resistance are then estimated, revealing quite good electrochemical performance of the LTO particles as an effective anode active material for lithium secondary batteries.

Lithium ion batteries have been extensively used in portable electronic devices due to their high energy density and long cycle life. Recently, lithium ion batteries are required to run conditions that drive up to 1.5C, 2.0C, or higher in order to produce quick charge secondary cells, but the life degradation and safety concerns and rising. In other words, as the number of repetitions of the charge and discharge increases, the binding between the active materials and the ionic conductors becomes loose, and the contact resistance between the particles increases, and due to the increased resistance of the electrode, the battery performance is degraded, and during the life cycle degradation of cathode and anode materials occurs, and it is directly linked to life and safety issues. This study aims to improve the quick charge performance by improving the lithium ion material.

In this study, a finite element analysis approach is proposed to predict the fluid-structure interaction behavior of active materials for lithium-ion batteries (LIBs), which are mainly composed of graphite powder. The porous matrix of graphite powder saturated with fluid electrolyte is considered a representative volume element (RVE) model. Three different RVE models are proposed to consider the uncertainty of the powder shape and the porosity. Pwave modulus from RVE solutions are analyzed based on the microstructure and the interaction between the fluid and the graphite powder matrix. From the results, it is found that the large surface area of the active material results in low mechanical properties of LIB, which leads to poor structural durability when subjected to dynamic loads. The results obtained in this study provide useful information for predicting the mechanical safety of a battery pack.

Lithium ion battery are one of representative rechargeable batteries with high energy density, tiny memory effect, and low self-discharge and composed of anode, cathode, electrolyte, and membrane separator. The importance of membrane separator has been improved further as electric vehicle market increases rapidly. The conventional membrane separators are based on polyolefin (e.g., polyethylene and/or polypropylene). In case of lithium ion battery with a high capacity, polyolefin membrane separators are suffering from low thermal resistance and easy short-circuit formation leading to overheating. For these reasons, in this study, gel polymers are in-situ synthesized in electrolytes used as solvent, which are located in pores of polyolefin separators to obtain gel polymer electrolyte-polyolefin reinforced membranes.

향후 우리 사회의 혁신적 변화를 가져올 휴대용 전자기기, 전기자동차 및 스마트 그리드 에너지 저장장치 등의 비약적인 발전에 따라, 그 전원으로서 리튬이차전지에 대한 관심이 더욱 증대하고 있다. 본 총설에서는, 리튬이차전지 핵심 소재 중 하나인 분리막에 대해 기공 구조 및 물리화학적 물성 관점에서 고찰하고, 이와 함께 최신 연구 동향을 소개하고자 한다. 리튬이차전지 분리막은 양극과 음극 사이에 위치하는 다공성 막으로서, 두 전극 간의 전기적 단락을 방지하고, 이온의 흐름을 가능하게 하는 기능을 갖는다. 분리막 자체는 전지 내 전기화학 반응에는 직접적으로 참여하지 않으나, 앞서 언급한 기능들에 의해 전지 성능 및 안전성에 큰 영향을 끼친다. 최근 들어, 이러한 분리막의 기본 특성 이외에, 전지 안전성 강화 및 금속 이온 흡착 등을 비롯한 다양한 기능 부여를 위한 노력들이 활발히 진행되고 있다. 본 총설에서는 현재 상업화된 폴리올 레핀 분리막에 대한 이해를 토대로, 개질 폴리올레핀 분리막, 부직포 분리막, 세라믹 복합 분리막 및 화학 활성 분리막 등으 로 대표되는 최신 분리막 기술들을, 차세대 전지 개발 방향과 관련 지어 기술하고자 한다.

The characteristics of aqueous lithium recovery by ion exchange were studied using three commercial cation exchange resins: CMP28 (porous type strong acid exchange resin), SCR-B (gel type strong acid exchange resin) and WK60L (porous type weak acid exchange resin). CMP28 was the most effective material for aqueous lithium recovery; its performance was even enhanced by modifying the cation with K+. A comparison to Na+ and H+ form resins demonstrated that the performance enhancement is reciprocally related to the electronegativity of the cation form. Further kinetic and equilibrium isotherm studies with the K+ form CMP28 showed that aqueous lithium recovery by ion exchange was well fitted with the pseudo-second-order rate equation and the Langmuir isotherm. The maximum ion exchange capacity of aqueous lithium recovery was found to be 14.28 mg/g and the optimal pH was in the region of 4-10.

Lithium-ion batteries (LIBs) are rapidly improving in capacity and life cycle characteristics to meet the requirements of a wide range of applications, such as portable electronics, electric vehicles, and micro- or nanoelectromechanical systems. Recently, atomic layer deposition (ALD), one of the vapor deposition methods, has been explored to expand the capability of LIBs by producing near-atomically flat and uniform coatings on the shell of nanostructured electrodes and membranes for conventional LIBs. In this paper, we introduce various ALD coatings on the anode, cathode, and separator materials to protect them and improve their electrochemical and thermomechanical stability. In addition, we discuss the effects of ALD coatings on the three-dimensional structuring and conduction layer through activation of electrochemical reactions and facilitation of fluent charge collection.

In this study, several kinds of active carbons with high specific surface area and micro pore structure were prepared from the coconut shell charcoal using chemical activation method. The physical property of prepared active carbon was investigated by experimental variables such as activating chemical agents to char coal ratio, flow rate of inert gas and temperature. It was shown that chemical activation with KOH and NaOH was successfully able to make active carbons with high surface area of 1900~2500 m2/g and mean pore size of 1.85~2.32 nm. The coin cell using water-based binder in the electrolyte of LiPF6 dissolved in mixed organic solvents (EC:DMC:EMC=1:1:1 vol%) showed better capacity than that of oil-based binder. Also, it was found that the coin cell of water-based binder shows an improved cycling performance and coulombic efficiency.

The microstructures and cyclic voltammograms of Al-Si/C nano-composites were investigated as the anode of lithium ion batteries. Al-Si nanoparticles were prepared by the arc-discharge method. Al-Si/C nanoparticles were obtained by coated Al-Si nanoparticles with the precursor of glucose (C6H12O6) as carbon source. It was indicated that the post carbon coating treatment can reduce Al2O3 film on Al-Si particles, and new phase Al4C3 formed in the process can activate the inactivated materials of electrode in a certain extent.

Silicon-carbon composite was prepared by the magnesiothermic reduction of mesoporous silica and subsequent impregnation with a carbon precursor. This was applied for use as an anode material for high-performance lithium-ion batteries. Well-ordered mesoporous silica(SBA-15) was employed as a starting material for the mesoporous silicon, and sucrose was used as a carbon source. It was found that complete removal of by-products (Mg2Si and Mg2SiO4) formed by side reactions of silica and magnesium during the magnesiothermic reduction, was a crucial factor for successful formation of mesoporous silicon. Successful formation of the silicon-carbon composite was well confirmed by appropriate characterization tools (e.g., N2 adsorption-desorption, small-angle X-ray scattering, X-ray diffraction, and thermogravimetric analyses). A lithium-ion battery was fabricated using the prepared silicon-carbon composite as the anode, and lithium foil as the counter-electrode. Electrochemical analysis revealed that the silicon-carbon composite showed better cycling stability than graphite, when used as the anode in the lithium-ion battery. This improvement could be due to the fact that carbon efficiently suppressed the change in volume of the silicon material caused by the charge-discharge cycle. This indicates that silicon-carbon composite, prepared via the magnesiothermic reduction and impregnation methods, could be an efficient anode material for lithium ion batteries.

nanotubes were successfully synthesized using an electrospinning technique followed by calcination in air. The nanotubes were the single phase nature of and consisted of approximately 14 nm nanocrystals. SEM and TEM characterizations demonstrated that uniform hollow fibers with an average outer diameter of around 124 nm and wall thickness of around 25 nm were successfully obtained. As anode materials for lithium ion batteries, the nanotubes exhibited excellent cyclability and reversible capacity of up to 25 cycles at as compared to nanoparticles with a capacity of . Such excellent performance of the nanotube was related to the one-dimensional hollow structure which acted as a buffer zone during the volume contraction and expansion of Sn.

Mass production-capable powder was synthesized for use as cathode material in state-of-the-art lithium-ion batteries. These batteries are main powder sources for high tech-end digital electronic equipments and electric vehicles in the near future and they must possess high specific capacity and durable charge-discharge characteristics. Amorphous silicone was quite superior to crystalline one as starting material to fabricate silicone oxide with high reactivity between precursors of sol-gel type reaction intermediates. The amorphous silicone starting material also has beneficial effect of efficiently controlling secondary phases, most notably . Lastly, carbon was coated on powders by using sucrose to afford some improved electrical conductivity. The carbon-coated cathode material was further characterized using SEM, XRD, and galvanostatic charge/discharge test method for morphological and electrochemical examinations. Coin cell was subject to 1.5-4.8 V at C/20, where 74 mAh/g was observed during primary discharge cycle.

Two different types of graphite, such as flake graphite (FG) and spherical graphite (SG), were used as anode materials for a lithium-ion secondary battery in order to investigate their electrochemical performance. The FG particles were prepared by pulverizing natural graphite with a planetary mill. The SG particles were treated by immersing them in acid solutions or mixing them with various carbon additives. With a longer milling time, the particle size of the FG decreased. Since smaller particles allow more exposure of the edge planes toward the electrolyte, it could be possible for the FG anodes with longer milling time to deliver high reversible capacity; however, their initial efficiency was found to have decreased. The initial efficiency of SG anodes with acid treatments was about 90%, showing an over 20% higher value than that of FG anodes. With acid treatment, the discharge rate capability and the initial efficiency improved slightly. The electrochemical properties of the SG anodes improved slightly with carbon additives such as acetylene black (AB), Super P, Ketjen black, and carbon nanotubes. Furthermore, the cyclability was much improved due to the effect of the conductive bridge made by carbon additives such as AB and Super P.

다공성 Poly(propylene) 분리막의 지지 하에 전해질 용액 (EC/DEC 1 : 1 혼합물 내의 LiPF6 1 M 용액) 내에서 DEGDMA [Di(ethylene glycol) dimethacrylate]의 70℃ 열중합을 통하여 겔 고분자 전해질(GPE)막이 합성 되었다. 합성된 겔 고분자 전해질막의 이온전도도 및 전기화학적 안정성은 AC 임피던스법 및 CV (cyclic voltametry)법에 의하여 측정 평가하였다. 겔 고분자를 전해질로, 그리고 양극 및 음극으로는 각각 LiMi0.8Co0.2O2 및 graphite로 이용하여 리튬이온전지(LIB)도 제작하였다. 열중합을 통하여 리튬 이온전지에 적합한 이온전도도(10 -3 S/cm 이상) 및 전기화학적 안정성을 보이면서 자체적인 성상을 유지하는 겔 고분자 전해질막을 얻을 수 있었다. 단량체 함량 5%의 전구체로 제작한 겔 고분자 전지는 단량체 함량이 7.0% 및 10.0%인 경우에 비하여 우수한 고율 및 충-방전 효율을 보였다.