Porous metals demonstrate not only excessively low densities, but also novel physical, thermal, mechanical, electrical, and acoustic properties. Thus, porous metals exhibit exceptional performance, which are useful for diesel particulate filters, heat exchangers, and noise absorbers. In this study, SUS316L foam with 90% porosity and 3,000 μm pore size is successfully manufactured using the electrostatic powder coating (ESPC) process. The mean size of SUS316L powders is approximately 12.33 μm. The pore properties are evaluated using SEM and Archimedes. As the quantity of powder coating increases, pore size decreases from 2,881 to 1,356 μm. Moreover, the strut thickness and apparent density increase from 423.7 to 898.3 μm and from 0.278 to 0.840 g/cm3, respectively. It demonstrates that pore properties of SUS316L powder porous metal are controllable by template type and quantity of powder coating.

Fe-Cr-Al powder porous metal was manufactured by using new electro-spray process. First, ultra-finefecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid(0.05~0.5% powders) was dispersed on Polyurethane foam through the electro-spray process. And then degreasing andsintering processes were conduced. In order to examine the effect of cell size (200 µm, 450 µm, 500 µm) in process,pre-samples were sintered for two hours at temperature of 1450˚C, in H₂ atmospheres. A 24-hour thermo gravimetricanalysis test was conducted at 1000˚C in a 79% N₂ + 21% O₂ to investigate the high temperature oxidation behavior ofpowder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased withincreasing cell size. In the 200 µm porous metal with a thinner strut and larger specific surface area, the depletion ofthe stabilizing elements such as Al and Cr occurred more quickly during the high-temperature oxidation compared withthe 450, 500 µm porous metals.

A new manufacturing process of Fe-Cr-Al powder porous metal was attempted. First, ultra-fine fecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid (0.05~0.5% powders) was dispersed on PU (Polyurethane) foam through the electrospray process. And then degreasing and sintering processes were conduced. In order to examine the effect of sintering temperature in process, pre-samples were sintered for two hours at temperatures of , , , and , respectively, in atmospheres. A 24-hour TGA (thermo gravimetric analysis) test was conducted at in a 79% +21% to investigate the high temperature oxidation behavior of powder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased with increasing sintering temperature (2.57% oxidation weight gain at sintered specimen). The high temperature oxidation mechanism of newly manufactured Fe-Cr-Al powder porous metal was also discussed.

A novel production method for porous metal components has been developed by applying powder space holder (PSH) method to metal powder injection molding (MIM) process. The PSH-MIM method has an industrial competitive advantage that is capable of net-shape manufacturing the micro-sized porous metal products with complicated shapes and controlled porosity and pore size. In this study, the small impeller with homogeneous micro-porous structure was manufactured by the PSH-MIM method. The effects of combinations in size and fraction of PMMA particle on dimensional tolerance and variation of sintered porous specimens were investigated. It was concluded that the PSH-MIM method could manufacture commercially microporous metal components with high dimensional accuracy.