To estimate the removal efficiency of TRU and rare earth elements in an oxide spent fuel, basic dissolution experiments were performed for the reaction of rare earth elements from the prepared simfuel with chlorination reagents in LiCl-KCl molten salt. Based on the literature survey, NH4Cl, UCl3, and ZrCl4 were selected as chlorination reagent. CeO2 and Gd2O3 powders were mixed with uranium oxide as a representative material of rare earth elements. Simfuel pellets were prepared through molding and sintering processes, and mechanically pulverized to a powder form. The experiments for the reaction of the simfuel powder and chlorination reagents were carried out in a LiCl-KCl molten salt at 500°C. To observe the dissolution behavior of rare earth elements, molten salt samples were collected before and after the reactions, and concentration analysis was performed using ICP. After the reaction completed, the remaining oxide was washed with water and separated from the molten salt, and XRD was used for structural analysis. As a result of salt concentration analysis, the dissolution performance of rare earth elements was confirmed in the reaction experiments of all chlorination reagents. In an experiment using NH4Cl and ZrCl4, the uranium concentration in the molten salt was also measured. In other words, it seemed that not only rare elements but also uranium oxide, which is a main component of simfuel, was dissolved. Therefore, it is thought that the dissolution of rare earth elements is also possible due to the collapse of the uranium oxide structure of the solid powder and the reaction with the oxide of rare earth elements exposed to molten salt. As a result of analyzing the concentration changes of Simfuel before and after each reaction, there was little loss of uranium and rare earth elements (Ce/Gd) in the NH4Cl experiment, but a significant amount of rare earth elements were found to be reduced in the UCl3 experiment, and a large amount of rare earth elements were reduced in the ZrCl4 reaction.

We report a method for preparing rare earth oxides (RexOy) from the recycling process for spent Ni-metal hydride (Ni-MH) batteries. This process first involves a leaching of spent Ni-MH powders with sulfuric acid at 90℃, resulting in rare earth precipitates (i.e., NaRE(SO4)2·H2O, RE = La, Ce, Nd), which are converted into rare earth oxides via two different approaches: i) simple heat treatment in air, and ii) metathesis reaction with NaOH at 70℃. Not only the morphological features but also the crystallographic structures of all products are systematically investigated using field-emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD); their thermal behaviors are also analyzed. In particular, XRD results show that some of the rare earth precipitates are converted into oxide form (such as La2O3, Ce2O3, and Nd2O3) with heat treatment at 1200℃; however, secondary peaks are also observed. On the other hand, rare earth oxides, RExOy can be successfully obtained after metathesis of rare earth precipitates, followed by heat treatment at 1000℃ in air, along with a change of crystallographic structures, i.e., NaRE(SO4)2·H2O → RE(OH)3 → RExOy.

Pyroprocessing에 의한 사용후핵연료 처리 과정에서 방사성 희토류 염화물이 포함된 폐용융염이 발생된 다. 이러한 폐 용융염 내에 존재하는 방사성 희토류 염화물을 산화물로 침전시켜 회수함으로서 용융염을 재 생할 수 있다. 최종적으로 발생되는 방사성 희토류 산화물의 저장과 처분에 적합한 monolithic 고화체를 제 조하기 위한 연구를 수행하였다. 본 연구에서는 고상 소결에 의해 붕규산 유리에 의한 고화체 제조, 희토류 산화물을 모나자이트로 합성한 후 붕규산 유리에 의한 고화체 제조를 수행하였다. 또한 zinc titanate 세라믹 이 주요성분인 고화 매질(ZIT)을 개발하여 고화체를 제조하였으며 각각의 고화체에 대한 침출 및 물리화학 적 특성을 비교 평가하였다. 고상 소결에 의해 제조된 ZIT 매질 고화체는 내 침출성이 크며 밀도가 크고 열전 도도가 우수한 특성을 나타내었다.