This study described a way of developing a resin for deviceizing quantum dots. Furthermore, the following conclusions were obtained by developing light curable syrup and UV curable syrup. First, The viscosity of the mixed resin decreased as the content of the diluent increased, and the value was bewteen 4,310 and 1,473cps. Second, haze was measured by using NDH 5000, and all of the synthesized syrups were obtained a haze value of 1% or less with a transmittance of 95% or more in the visible light region. Third, the viscosity of the mixed resin decreased as the temperature increased, and at this point, the viscosity showed a value of 4,219 to 1,128cps. Lastly, As a result of measuring the viscosity of the resin before and after mixing the quantum dot nanoparticles, it appears to be little change.

In this study, a mixed resin containing Bis-GMA was developed to produce a light-emitting sign using quantum dots. As a result of measuring the viscosity, color coordinates change, and luminance of the mixed resin, the following conclusions were obtained. The viscosity of the mixed resin decreased as the content of the diluent increased, and viscosity values ​​ranged from 3,627 to 1,349cps showed as a result. The viscosity of the mixed resin decreased as the temperature increased, and the viscosity showed a value of 5,156 to 1,132cps. For the optical properties of InP/GaP/ZnSe/ZnS quantum dots, the absolute quantum efficiency was 91% at 522nm and 90% at 618nm when the gallium was 0.01%. The luminance of the light-emitting sign using the resin mixed with quantum dots was showed 142.6cd/m2 in white and 104.2cd/m2 in the red region.

In this study, a mixed resin containing Bis-GMA was developed to produce a light-emitting sign using quantum dots. As a result of measuring the viscosity, color coordinates change, and luminance of the mixed resin, the following conclusions were obtained. The viscosity of the mixed resin decreased as the content of the diluent increased, and viscosity values ​​ranged from 3,627 to 1,349cps showed as a result. The viscosity of the mixed resin decreased as the temperature increased, and the viscosity showed a value of 5,156 to 1,132cps. For the optical properties of InP/GaP/ZnSe/ZnS quantum dots, the absolute quantum efficiency was 91% at 522nm and 90% at 618nm when the gallium was 0.01%. The luminance of the light-emitting sign using the resin mixed with quantum dots was showed 142.6cd/m2 in white and 104.2cd/m2 in the red region.