        1.
        2013.09 KCI 등재 구독 인증기관 무료, 개인회원 유료
        For this research, prepared water soluble milk casein resin and waterborne polyurethane-acrylic resin. Use these resin, this article has been analyzed about change of mechanical properties by increasing amount of casein resin in polyurethane-acrylic resin on coated leather. According to measure data for solvent resistance, WPA(waterborne polyurethane-acrylic resin) resin and WPA-C1, C2, C3(samples of polyurethane-acrylic resin with milk casein resin) had good property. As known in the results, increase of casein constant did not influence to big change of hybrid resin properties. As test of tensile strength, WPA had lowest tensile characteristic(1.598 kgf/㎟) and WPA-C3 had highest tensile characteristic(1.718 kgf/㎟). Also best properties of abrasion was WPA-C3(06.021 ㎎.loss). In elongation case, WPA had best properties(754 %) in this experiment.
        4,000원
        2.
        2011.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        In this study we experimented that how chain extension influences to waterborne urethane-acrylic hybrid resin for leather garment coatings. We knew that polyurethane-acrylic hybrid resins had 5 grades of solvent resistance. Tensile strength measured in the polyurethane-acrylic resin(EDA 5.37 g, 1.928 kgf/mm2) had the most strong strength. Also polyurethane-acylic hybrid resin(EDA 5.37 g. 30.2 mg. loss) had better result than other hybrid resins. EDA contents higher, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-acrylic hybrid resin showed the effect in leather coating with ratio of EDA.
        4,000원
        3.
        2010.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        In this study, we experimented that how to synthesis waterborne urethane-acrylic hybrid resin for leather coatings. First of all, We had analyzed data by FT-IR, SEM and TGA for the machanical properties. By TGA analysis polymers showed heat distortion temperature. and by FT-IR measurement we confirmed that synthesis of urethane and acrylic. In the experiment, solvent resistance, polyurethane and acrylic grades 4-5 showed both a high. Tensile strength measured in the waterborne polyurethane 〉 Acrylic emulsion showed strength in the order. Films were obtained by coating the water born resin on leveled surfaces and allowing them to dry at room temperature for 72hrs. After demolding, the films were kept in a desiccator to avoid moisture contant at 25℃ for 45hrs before the measurements. In this result, the mechanical propersies of waterborne polyurethane-acrylic hybrid resin showed that how effect to resin in leather coating between polyurethane content and acrylic content. Therefore, acrylic emulsion had most high solvent resistance glade and waterborne polyurethane had good result in abrasion test and tensile strength.
        4,000원