Recently, nanotubes have considerably researched because of their novel application about photocatalysis, dye-sensitized solar cells (DSSCs), lithium ion battery, etc. In this work, self-standing nanotube arrays were fabricated by anodic oxidation method using pure Ti foil as a working electrode in ethylene glycole with 0.3M + . Growth behavior of nanotube arrays was compared according to temperature, voltage and time. The morphology, structure and crystalline of anodized nanotube arrays were observed by FE-SEM (field emission scanning electron microscope) and XRD (X-ray diffraction).

Self-standing TiO2 nanotube arrays were fabricated by potentiostatic anodic oxidation method using pure Ti foil as a working electrode and ethylene glycol solution as electrolytes with small addition of NH4F and H2O. The influences of anodization temperature and time on the morphology and formation of TiO2 nanotube arrays were investigated. The fabricated TiO2 nanotube arrays were applied as a photoelectrode to dye-sensitized solar cells. Regardless of anodizing temperature and time, the average diameter and wall thickness of TiO2 nanotube show a similar value, whereas the thickness show a different trend with reaction temperature. The thickness of TiO2 nanotube arrays anodized at 20℃ and 30℃ was time-dependent, but on the other hand its at 10℃ are independent of anodization time. The conversion efficiency is low, which is due to a morphology breaking of the TiO2 nanotube arrays in manufacturing process of photoelectrode.

In this work, the effect of anodic oxidation treatment on Cr(VI) ion adsorption behaviors of activated carbon fibers (ACFs) was investigated. The aqueous solutions of 10 wt% H3PO4 and NH4OH were used for acidic and basic electrolytes, respectively. Surface characteristics and textural properties of ACFs were determined by XPS and N2 adsorption at 77 K. The heavy metal adsorption of ACFs was conducted by ICP. As a result, the adsorption amount of the anodized ACFs was improved in order of B-ACFs 〉 A-ACFs 〉 pristine-ACFs. In case of the anodized treated ACFs, the specific surface area was decreased due to the pore blocking or pore destroying by acidic electrolyte. However, the anodic oxidation led to an increase of the Cr(VI) adsorption, which can be attributed to an increase of oxygen-containing functional groups, such as, carboxylic, lactonic, and phenolic groups. It was clearly found that the Cr(VI) adsorption was largely influenced by the surface functional groups, in spite of the reduced specific surface area of the ACFs.

The surface treatment of C-type isotropic pitch-based carbon fiber was carried out by anodic oxidation in 5 wt% NH4NO3 electrolyte. The changes of fiber surface and carbon fiber/ABS resin composites were characterized by SEM, XPS and mechanical properties test. The oxygen functional groups on the surface, such as hydroxyl (-C-OH), carboxyl (-COOH) groups etc., increased after oxidation. Tensile strength, flexural strength and modulus of carbon fiber/ABS composites were also enhanced. However, the impact strength decreased with the improvement of the surface adhesion between CF and matrix.

양극산화법을 이용하여 광촉매 특성을 나타내는 TiO2 피막을 제조하고 염료의 분해반응을 통하여 광분해 효율을 조사하였다 양극산화법에 의해 제조된 산화피막은 모두 광촉매 분해특성이 있었으며 양극산화의 조건에 따라서 TiO2 피막의 성장거동과 피막 형태에 차이가 나타났다. 황산용액에서 양극산화된 TiO2 피막은 불규칙적 인 입자모양으로 anatase와 rutile이 혼합된 조직이었으며, 인산이 첨가된 혼합용액에서 형성된 TiO2는 anatase로 셀 모양의 피막형태로 생성되었다. 광촉매 특성에 적합한 양극산화의 인가 전압은 180V인 것으로 나타났다.