Anti-reflection thin films are fabricated on glass substrates using the screen printing method. Tetra ethyl silicate(TEOS) and methyl tri methoxy silane(MTMS) are used as starting materials and buthyl carbitol acetate(BCA) and buthyl cellusolve(BC) are mixed to improve the viscosity of the solution. Anti-reflection thin films are fabricated according to the number of the screen mesh and the characteristics improve as the mesh size increases. The transmittance and reflectance of the coated thin film using 325 mesh are about 94 % and 0.43 % in the visible wavelength. The thickness and refractive index of the AR thin film are 107 nm and n = 1.26, respectively.

Anti-reflection coating films have used to increase the transmittance of displays and enhance the efficiency of solar cells. Hydrophobic anti-reflection coating films were fabricated on a glass substrate by sol-gel method. To fabricate an anti-reflection film with a high transmittance, poly ethylene glycol (PEG) was added to tetraethyl orthosilicate (TEOS) solution. The content of PEG was changed from 1 to 4 wt% in order to control the morphology, thickness, and refractive index of the SiO2 thin films. The reflectance and transmittance of both sides of the coated thin film fabricated with PEG 4 wt% solution were 0.3% and 99.4% at 500 nm wavelength. The refractive index and thickness of the thin film were n = 1.29 and d = 105 nm. Fluoro alkyl silane (FAS) was used for hydrophobic treatment on the surface of the anti-reflection thin film. The contact angle was increased from 13.2˚ to 113.7˚ after hydrophobic treatment.

VO2 써모크로믹 원도우의 가시광 투과율을 높히기 위하여 내마모성이 우수한 SiO2박막을 이용하여 AR(anti-rdflection)코팅을 하였다. 두가지 중요한 공정변수인 기판온도와 증착속도가 AR효과에 미치는 영향을 조사하였다. 그리고 SiO2박막의 AR효과는 낮은 기판온도와 높은 증착속도에서 더 우수한 것으로 나타났으며, 이는 SiO2AR 박막의 굴절율과 상관관계가 있는 것으로 나타났다. VO2 써모크로믹 유리 위에 SiO2AR-코팅을 했을 때 약 30% 정도의 가시광 투과율의 향상이 있었다. 그리고 AR-코팅을 하지 않은 경우보다 더 뚜렷한 써모크로미즘을 나타냈다. 또한 천이온도는 70˚C정도로 AR-코팅을 하지 않은 VO2써모크로믹 유리의 경우와 같게 나타났다.