Lilium dauricum is a rare and endangered species belonging to the family Liliaceae. The species contains several bioactive compounds used as functional foods and medicinal agents in Northeast Asia. This study aimed (1) to establish an in vitro bulblet culture using an air-lift bioreactor and callus culture for the conservation of L. dauricum and obtaining its bioactive compounds; (2) investigate the plant phenolic compounds from both cultures system. The highest bulblet production with 12.5-fold increase in growth rate was obtained using MS medium supplemented with 0.5 g L-1 BA and 3% sucrose. Addition of 7% sucrose facilitated bulblet enlargement, with approximate 2.5- and 7-fold increases in diameter and fresh weight, respectively. The highest rate of callus (100%) was obtained using a combination of 1.0 mg L-1 picloram and 0.5 mg L-1 Kinetin. The callus proliferation occurred on MS medium supplemented with 1.0 mg L-1 picloram, 0.25 mg L-1 kinetin, and 0.25 g L-1 casein hydrolysate. There was a significant difference in the total phenolic compound content of callus, which was 1.5-fold higher than that in the bulblets. These findings indicate a suitable system for optimizing both bulblet and callus culture of L. dauricum, therefore, providing useful bio-materials for industrial purposes and contributing to the conservation of this species.

Ti and Ti alloys have been extensively used in the medical and dental fields because of their good corrosion resistance, high strength to density ratio and especially, their low elastic modulus compared to other metallic materials. Recent trends in biomaterials research have focused on development of metallic alloys with elastic modulus similar to natural bone, however, many candidate materials also contain toxic elements that would be biologically harmful. In this study, new Ti based alloys which do not contain the toxic metallic components were developed using a theoretical method (DV-Xα). In addition, alloys were developed with improved mechanical properties and corrosion resistance. Ternary Ti-Ag-Zr alloys consisting of biocompatible alloying elements were produced to investigate the alloying effect on microstructure, corrosion resistance, mechanical properties and biocompatibility. The effects of various contents of Zr on the mechanical properties and biocompatibility were compared. The alloys exhibited higher strength and corrosion resistance than pure Ti, had antibacterial properties, and were not observed to be cytotoxic. Of the designed alloys' mechanical properties and biocompatibility, the Ti-3Ag-0.5Zr alloy had the best results.

Titanium and its alloys are useful for implant materials. In this study, porous Ti-Nb-Zr biomaterials were successfully synthesized by powder metallurgy using a NH4HCO3 as space holder and TiH2 as foaming agent. Consolidation of powder was accomplished by spark plasma sintering process(SPS) at 850˚C under 30 MPa condition. The effect of high energy milling time on pore size and distribution in Ti-Nb-Zr alloys with space holder(NH4HCO3) was investigated by optical microscope(OM), scanning electron microscope(SEM) & energy dispersive spectroscopy(EDS) and X-ray diffraction(XRD). Microstructure observation revealed that, a lot of pores were uniformly distributed in the Ti-Nb-Zr alloys as size of about 30-100μm using mixed powder and milled powders. In addition, the pore ratio was found to be about 5-20% by image analysis, using an image analyzer(Image Pro Plus). Furthermore, the physical properties of specimens were improved with increasing milling time as results of hardness, relative density, compressive strength and Young's modulus. Particularly Young's modulus of the sintered alloy using 4h milled powder reached 52 GPa which is similar to bone elastic modulus.

To improve coating ability and the life of the coating, Ti based composite materials with hydroxyapatite(HA) should be developed. The raw materials of Ti-26wt%, Nb-1wt%, and Si with 10wt% HA were mixed for 24 h by a mixing machine and milled for 1 h to 6 h by planetary mechanical ball milling. Ti-26%Nb-1%Si-(10%HA) composites, composed of nontoxic elements, were fabricated successfully by spark plasma sintering(SPS) at 1000˚C under 70MPa. The relative density of the sintered Ti-Nb-Si-HA composites using the 24 h mixed powder, and the 6 h milled powder, was 91% and 97 %, respectively. The effects of HA contents and milling time on microstructure and mechanical properties were investigated by SEM and hardness tester, respectively. The Vickers hardness of the composites increased with increasing milling time and higher HA content. The Young's modulus of the sintered Ti-26%Nb-1%Si-10%HA composite using the 6 h-milled powder was 55.6 GPa, as obtained by compression test. Corrosion resistance of the Ti-26wt%Nb-1wt%Si composite was increased by milling and by the addition of 10wt%HA. Wear resistance was improved with increasing milling time. Biocompatibility of the Ti-Nb-Si alloys was improved by the addition of HA.

The Ti-6Al-4V extra low interstitial (ELI) alloy has been widely used as an orthopedic implant material because of its excellent mechanical properties and biocompatibility. However, it still has many problems, including a high elastic modulus and toxicity of the Al and V elements. Therefore, non-toxic biomaterials with a low elastic modulus need to be developed. A high energy mechanical milling (HEMM) process is introduced to improve the effect of sintering. Rapid sintering of spark plasma sintering (SPS) under pressure was used to make an ultra fine grain of Ti-25 wt.%Nb-7 wt.%Zr-10 wt.%Mo-(10 wt.%CPP) composites with bio-attractive elements for increasing strength. These composites were fabricated by SPS at 1000˚C at 60 MPa using HEMM powders. During the sintering process, CaTiO3, TixOy, and CaO were formed because of the reaction between Ti and CPP. The effects of CPP content on the physical and mechanical properties of the sintered Ti-Nb-Zr-Mo-CPP composites were investigated. The biocompatibility and corrosion resistance of the Ti-Nb-Zr-Mo alloys were improved by the addition of CPP.

Ti-6Al-4V ELI (Extra Low Interstitial) alloy have been widely used as alternative to bone due to its excellent biocompatibility, although it still has many problems such as high elastic modulus and toxicity. Therefore, biomaterials with low elastic modulus and non toxic characteristics have to be developed. A novel β Ti-35wt%Nb-7wt%Zr-Calcium pyrophosphate (CPP) composite that is a biocompatible alloy without elemental Al or V was fabricated by spark plasma sintering (SPS) at 1000˚C under 70 MPa using high energy mechanical milled (HEMM) powder. The microstructure and phases of the milled powders and the sintered specimens were studied using SEM, TEM, and XRD. Ti-35wt%Nb-7wt%Zr alloy was transformed from α phase to β phase in the 4h-milled powder by sintering. The sintered specimen using the 4h-milled powder showed that all the elements were distributed very homogeneously and had higher density and hardness. β Ti alloy-CPP composite, which has nanometer particles, was fabricated by SPS using HEMMed powder. During the sintering process, CaTiO3, TixOy, and CaO were formed because of the reaction between Ti and CPP. The Vickers hardness of the composites increases with the increase of the milling time and the addition of CPP. The biocompatibility of the Ti-Nb-Zr alloys was improved by addition of CPP.

Ti-6Al-4V ELI (Extra Low Interstitial) alloy has been widely used as an alternative to bone due to its excellent biocompatibility. However, it still has many problems, including a high elastic modulus and toxicity. Therefore, nontoxic biomaterials with a low elastic modulus should be developed. However, the fabrication of a uniform coating is challenging. Moreover, the coating layer on Ti and Ti alloy substrates can be peeled off after implantation. To overcome these problems, it is necessary to produce bulk Ti and Ti alloy with hydroxyapatite (HA) composites. In this study, Ti, Nb, and Zr powders, which are biocompatible elements, were milled in a mixing machine (24h) and by planetary mechanical ball milling (1h, 4h, and 6h), respectively. Ti-35%Nb-7%Zr and Ti-35%Nb-7%Zr-10%HA composites were fabricated by spark plasma sintering (SPS) at 1000˚C under 70MPa using mixed and milled powders. The effects of HA addition and milling time on the biocompatibility and physical and mechanical properties of the Ti-35%Nb-7%Zr-(10%HA) alloys have been investigated. Ti2O, CaO, CaTiO3, and TixPy phases were formed by chemical reaction during sintering. Vickers hardness of the sintered composites increases with increased milling time and by the addition of HA. The biocompatibilty of the HA added Ti-Nb-Zr alloys was improved, but the sintering ability was decreased.

Porous titanium implants can be produced by powder metallurgy in combination with suitable space holder materials. Various mechanical experiments were done to characterize this material regarding the influence of the processing parameters on microstructure and mechanical properties taking into account the properties of the human bone. In this paper, the anistropic behaviour of uniaxially compacted samples was analysed in compression tests and compared to the behaviour of isostatically pressed samples. The failure of the struts of the porous titanium and the crack- initiation and -growth was examined by in-situ SEM analysis.

Porous TiNi bodies were produced by Self-propagating High-temperature Synthesis (SHS) method from a powder mixture of Ti and Ni. Porosity, pore size and structure, mechanical property, and transformation temperature of TiNi product were investigated. The average porosity and pore size of produced porous TiNi body are 63% and , respectively. XRD analysis showed that the major phase of produced TiNi body is B2 phase. Its average fracture strength and elastic modulus measured under dry condition were MPa and GPa, respectively. It could be strained up to 7.3 %. The transformation temperatures determined by DSC showed the temperature of and temperature of .

Production of Bacterial Cellulose (BC) by Gluconacetobacter sp. A5 was studied in shaken culture using different cost-effective carbon sources and its structural and mechanical properties were evaluated. Glycerol showed the highest level (7.26 g/l) of BC production, which was about three times higher than the yield in glucose medium. BC production depended not only on the decrease in pH, but also on the ability of Gluconacetobacter sp. A5 to synthesize glucose from different carbon sources and then polymerize it into BC. All BC produced from different carbon sources exhibited a three-dimensional reticulated structure consisting of ultrafine cellulose fibriles. Carbon sources did not significantly change the microfibrile structure of the resulting BC. BC produced from glucose medium had the lowest water-holding capacity, while BC from molasses medium had the highest. XRD data revealed that all BC were cellulose type І, the same as typical native cellulose. The crystalline strength of BC produced in glucose medium was the highest, and that in molasses medium was the lowest. Our results suggest that glycerol could be a potential low-cost substrate for BC production, leading to the reduction in the production cost, and also to produce BC with different mechanical properties by selecting appropriate carbon source.