In the present study the microstructure of low-carbon steels fabricated by controlled rolling and accelerated cooling processes was characterized and identified based on various microstructure analysis methods including optical and scanning electron microscopy, and electron backscatter diffraction(EBSD). Although low-carbon steels are usually composed of α-ferrite and cementite(Fe3C) phases, they can have complex microstructures consisting of ferrites with different size, morphology, and dislocation density, and secondary phases dependent on rolling and accelerated cooling conditions. The microstructure of lowcarbon steels investigated in this study was basically classified into polygonal ferrite, acicular ferrite, granular bainite, and bainitic ferrite based on the inverse pole figure, image quality, grain boundary, kernel average misorientation(KAM), and grain orientation spread(GOS) maps, obtained from EBSD analysis. From these results, it can be said that the EBSD analysis provides a valuable tool to identify and quantify the complex microstructure of low-carbon steels fabricated by controlled rolling and accelerated cooling processes.

결정립 미세화는 강도와 인성을 동시에 향상시킬 수 있는 유일한 방법이다. 제어압연과 가속냉각은 공정 중에 재결정과 결정립 조대화 거동을 조절함으로써 기계적 성질을 향상시키는 효과적인 방법으로 알려져 있으며, 반복열처리에 의한 반복상변태는 결정립 미세화 방법 중의 하나이다. 본 연구에서는 제어압연과 반복열처리를 복합 적용하여 그 효과를 관찰하였다. Mo 첨가효과와 공정변수의 효과를 관찰하기 위해 Mo이 첨가된 저탄소강 시편을 준비하여 Gleeble로 가공열처리 모의실험을 하였다. Mo첨가는 결정립 조대화 온도를 상승시키고, 오스테나이트 재결정을 억제하는 효과를 나타내었다. 오스테나이트 결정립 미세화에 가장 효과적인 공정조건은 반복 열처리 제어압연을 두번 실시하는 것이고, 첫번째보다 두번째 압연율을 더 크게 하는 것이었다