Solvent-free low foaming scouring agents (LFSC) were prepared by blending of 2-ethylhexylaminoethyl sulfate (2-EHAS), POE(10) octadecylbenzyl- ammonium chloride (POBAC) and Sedlan FF-200 (FF-200). As the results of several tests, 2-EHAS/POBAC/FF-200/water (8g/12g/20g/60g) mixture (LFSC-5) showed good cleaning power, penetrating ability and stability to alkali, and gave less problem in water pollution. The foaming power of LFSC-5 measured by Ross and Miles method was 8mm foam height immediately after foaming, and that measured by Ross and Clark method was less than 300mm foam height at 30℃, and 18mm at 80℃. As a result, LFSC-5 proved a good low foaming scouring agent for fiber.

Low foaming scouring agents (LSSA) were prepared by blending of amine salt of dodecylbenzene sulfone, poly (PO-b-EO) glycol, Newpol PP-2000, MJU-100, ethylene glycol and organic solvent. As the results of several tests, LSSA-2 showed good scouring effect, penetrating ability and emulsifiability, and showed not much water pollution. The foaming power of LSSA-2 measured by Ross & Miles method was 11mm foam height immediately after foaming. And the foaming power of LSSA-2 measured by Ross & Clark method were less than 310mm foam height at 30℃, 17mm at 80℃. As a result, LSSA-2 was proved as a good foaming scouring agent.

Low foaming acidic degreasing agent(LFADAs) were prepared by blending sorbitol, n-octanoic acid, MJU-100A, Tetronix T-701, Na-dioctyl sulfosuccinate, Demol C, and phosphoric acid. The physical properties of LFADAs tested with aluminum specimen showed the following results ; when 3wt% LFADA-6 was performed at 70℃, the degreasing rate was 95% which is comparitively good, and the percentage of etching was 0.275% which was found to be less than that of commercialized product. When 20wt% of LFADA-6 was added at 65℃, the percentage of derusting was 92% and the good defoaming effect proved by following low foaming power tests respectively : Ross and Miles, and Ross and Clark methods.