The effect of electrochemical surface treatments in KOH chemical solution on microstructures of carbon blacks was investigated in terms of surface functional values and XRD measurements. And their mechanical interfacial properties of the carbon blacks/rubber composites were studied by the composite tearing energy (GIIIC). It was found that the development of basic-surface functional groups lead to the significant physical changes of carbon blacks, such as, decrease of the interlayer spacing (d002), increase of the crystalline size along c-axis (Lc), and increase of degree of crystalline (χc). This treatment is possibly suitable for carbon blacks to be incorporated in a hydrocarbon rubber matrix, resulting in improving the hardness and tearing energy of the resulting composites.

본 연구에서는 부분산화한 Ti 분말을 첨가한 BaTiO3계 세라믹스를 진공중 1350˚C에서 1 h 소결하여 제조하였다. 공기중 가열후 전기적 성질과 미세조직에 미치는 부분산화한 Ti분말 첨가량의 효과를 조사하였다. 그 결과, 5~7vol%의 부분산화한 Ti분말을 첨가한 반도성 BaTiO3계 세라믹스는 비정항의 변화크기가 105이상인 우수한 PTCR 특성을 나타내었고 또한, 고다공질과 미립화된 조직을 얻을 수 있었다. 5 vol%의 부분산화한 Ti 분말을 첨가한 BaTiO3계 세라믹스의 상대밀도와 입도는 각각 54%, 1.3 μm였다. 부분산화한 Ti 분말의 첨가에 의한 BaTiO3계 세라믹스의 PTCR 특성 발현은 입계에서의 산소 흡착에 기인하였는데, 이는 Heywang모델로써 설명할 수 있었다.

고밀도 DRAM에서 박막 커패시터로의 적용을 위해 Zr이 첨가된 (Ba(sub)1-x, Sr(sub)x)TiO3<원문차조> 박막이 r.f. magnetron sputter-ing 법에 의해 제조되었다. 증착된 박막들은 다결정질 구조를 보였으며 증착압력이 감소함에따라 Zr/Ti의 비가 현저히 증가하였으며 본 연구에서는 얻어진 박막들은 100kHz에서 380∼525의 유전상수값을 나타냈다. 전압에 따른 커패시턴스와 분극량의 변화는 이력특성을 크게 보이지 않아 상유전상으로 형성되었음을 보였다. 누설전류밀도는 증착압력이 감소함에 따라 작아지는 경향을 보였고 10mTorr이상에서 증착된 박막의 경우 200kV/cm의 전계에서 10(sup)-7∼10(sup)-8A/cm2의 차수를 갖는 누설전류밀도를 보여 본 연구에서 제조된 (Ba(sub)1-x, Sr(sub)x)(Ti(sub)1-x, Zr(sub)x)O3<원문참조>박막은 고밀도 DRAm을 위한 커패시터에의 적용가능성을 보였다.

A process has been successfully used to manufacture 6061/Graphite composite material and the Graphite particles are distributed uniformly within the Al alloy matrix. The 6061 powders was mixed with natural Graphite particles in a ball milling blender and cold compacted specimens were extruded into rods 15mm in diameter at 450. The results showed that tensile properties of the composites with Graphite content have been reduced. The emergence of fine microstructures appeared to be related to the graphite volume. Heat-treated composites were found to possess good mechanical properties as compared with those of non heated composites. A model was used that the tensile strength of the composites would be estimated from the theoretical calculation and experimental data.

전해콘텐서용 알루미늄박을 ammonium adipate 용액을 이용하여 65˚C에서 10분간 100V 및 140V로 각각 양극 산화시켜 산화 알루미늄 유전체를 만들었다. 유전층의 두께, 화학양론적 관계, 결정구조 등을 RBS 및 TEM을 이용하여 분석하였고, 알루미늄박의 에칭시 황산 첨가로 인한 표면적의 변화는 임피던스 분석법으로 조사 하였다. 생성된 유전피막은 100V 및 140V의 전압을 사용했을 경우 각각 약 130nm 및 190nm 두께의 비정질로 나타났으며 피막의 알루미늄과 산소원소의 화학양자론적 비는 약 2:3의 비율로 존재했다. 또한 유전피막은 전자빔은 조사에 의해 쉽게 γ-Al2</TEX>O3 형태의 결정질로 변태 되었다. 염산 에칭욕에 황산 첨가시 나타나는 알루미늄박의 표면변화는 임피던스 분석결과와 정전 용략의 변화가 일치하는 경향을 나타냈다.

초미립 BaTiO3분말을 출발물질로 하고 La3+을 0~2 mol% 첨가하여 1200~1400˚C에서 소결하였을 때 La3+을 첨가하지 않고 1350˚C 이상에서 소결한 경우를 제외하고는 모두 110~240 nm의 평균입경을 갖는 초미립의 La3+-doped BaTiO3소결체를 얻을 수 있었다. 이 때, 평균입경이 240 nm에서 110 nm로 감소함에 따라 정방정비 (c/a), 90˚ 분역의 부피분율, 상온 비유전율, 상전이온도(TC)에서의 최대 비유전율, TC 에서의 상전이 완만화도 등은 모두 감소하였다. 이와 같은 유전특성의 입경 의존성은 평균입경 감소에 따른 90˚ 분역 생성의 억제 및 그에 따른 내부응력의 영향으로 해석하였다.

The pure Ti, Ni and carbon powders were reaction milled to synthesize the TiC-Ni based cermet powders with ultrafine microstructures. After milling, the ultrafine TiC or amorphous Ti-Ni phase was obtained, respectively, according to the milling condition. The effects of milling variables on the synthesizing behavior of the powders were investigated in detail. The sintered TiC-Ni based cermet of the reaction milled powders consisted of very fine TiC of 0.2~1.5m, as compared with that of a commercial cermet of 3~5m. This demonstrates the potenial of reaction milling as an effective processing route for the preparation of cermet materials.

NiAl intermetallic compound has been tested as a binder phase, in order to improve the oxidation resistance and the mechanical properties of TiC-Ni cermet at a high temperature. The wettability of on TiC and the optimum sintering condition were investigated in TiC-(30, 40) vol% cermets with the sintering temperature (1380~) and time (30~99 min). The results are summarized as follows: 1) NiAl showed good wettability on TiC above ; 2) The shrinkages of the specimens increased with the sintering temperature, the sintering time and the binder content, whereas the relative densities were decreased; 3) Any other phase did not appeared in the microstructures of all sintered cermets. The grain sizes of TiC became larger as the sintering temperature and the sintering time as well as the binder content increased; 4) The hardness of the cermets decreased with increase in the sintering temperature and the sintering time as well as the binder content; 5) The transverse-rupture strength of the cermets increased with the sintering temperature and the sintering time, whereas it decreased with the binder content.

The microstructures and mechanical properties of submicron WC-Co cemented carbides were investigated in relation to cobalt content. To inhibit the WC grain growth during sintering, VC was added as a inhibitor in each alloy with 3 mass% to the cobalt content. The WC-(5, 8, 10, 15, 20) mass% Co compacts were sintered at for 30 min in vacuum. Some of WC-(5, 8, 10) mass% Co sintered compacts were HIPed with 120 atm at 130 for 1 hr. The shrinkages of all HIPed alloys were increased without depending on the cobalt contents and the sintered densities of them. The relative densities of the alloys were increased with the cobalt content and HIPing. The less the cobalt content, the larger the WC grain. Many contiguities of WC grains were found in WC-5 mass% Co alloy. The sizes and numbers of pores in the alloys were decreased by HIPing. And also the strength and the hardness of each alloy were increased. The maximum hardness was about 18.95 GPa in the WC-5 mass% Co alloy HIPed and the maximum transverse-rupture strength (T.R.S.) 3.2 GPa in the WC-20 mass% Co alloy sintered.

transition metals(Cu, Co)/ZSM-5 catalyst was made by mechanical alloying method, and their microstructures and repeated usage-properties were investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The conversions ability of NO in the catalyst was measured. A part of ZSM-5 in CO/ZSM-5 composite powders was amorphous and the amorphous phase became less stable with increasing Co content. Conversion ability of NO in 10Cu/ZSM-5 powders decreased from 89% to 12% and that in 10Co/ZSM-5 decreased from 22% to 17% by 7 times conversion tests.