본 연구에서는 상전이법을 이용하여 P(VDF-co-HFP) 분리막의 구조를 조절하였다. Macrovoid 없는 구조를 얻기 위하여 다양한 조건에서 비용매유도상전이(NIPS) 공법으로 분리막을 제막하였으나 고분자의 낮은 결정화 속도로 인해 macrovoid가 생성된다는 것을 관측하였다. 이를 극복하기 위해 증발유도상전이법(EIPS)과 증기유도상전이법(VIPS)을 도입하였으며 NIPS공법과 함께 제막되었을 때 이상적인 구조를 얻을 수 있다는 것을 확인하였다.

본 연구에서는 상전이법을 이용하여 P(VDF-co-HFP) 분리막의 구조를 조절하였다. Macrovoid 없는 구조를 얻기 위하여 다양한 조건에서 비용매유도상전이(NIPS) 공법으로 분리막을 제막하였으나 고분자의 낮은 결정화 속도로 인해 macrovoid가 생성된다는 것을 관측하였다. 이를 극복하기 위해 증발유도상전이법(EIPS)과 증기유도상전이법(VIPS)을 도입하였으 며 NIPS공법과 함께 제막되었을 때 이상적인 구조를 얻을 수 있다는 것을 확인하였다.

In this study, we investigated the overpotential of precipitation related to the catalytic activity of electrodes on the initial process of electrodeposition of Co and Co-Ni alloys on polycrystalline Cu substrates. In the case of Co electrodeposition, the surface morphology and the magnetic property change depending on the film thickness, and the relationship with the electrode potential fluctuation was shown. Initially, the deposition potential(−170 mV) of the Cu electrode as a substrate was shown, the electrode potential(Edep) at the Ton of electrodeposition and the deposition potential(−600 mV) of the surface of the electrodeposited Co film after Toff and when the pulse current was completed were shown. No significant change in the electrode potential value was observed when the pulse current was energized. However, in a range of number of pulses up to 5, there was a small fluctuation in the values of Edep and Eimm. In addition, in the Co-Ni alloy electrodeposition, the deposition potential(−280 mV) of the Cu electrode as the substrate exhibited the deposition potential(−615 mV) of the electrodeposited Co-Ni alloy after pulsed current application, the Edep of electrodeposition at the Ton of each pulse and the Eimm at the Toff varied greatly each time the pulse current was applied. From 20 % to less than 90% of the Co content of the thin film was continuously changed, and the value was constant at a pulse number of 100 or more. In any case, it was found that the shape of the substrate had a great influence.

Particle morphology change and different experimental condition analysis during composite fabrication process by traditional ball milling with discrete element method (DEM) simulation were investigated. A simulation of the three dimensional motion of balls in a traditional ball mill for research on the grinding mechanism was carried out by DEM simulation. We studied the motion of the balls, the ball behavior energy and velocity; the forces acting on the balls were calculated using traditional ball milling as simulated by DEM. The effect of the operational variables such as the rotational speed, ball material and size on the flow velocity, collision force and total impact energy were analyzed. The results showed that increased rotation speed with interaction impact energy between balls and balls, balls and pots and walls and balls. The rotation speed increases with an increase of the impact energy. Experiments were conducted to quantify the grinding performance under the same conditions. Furthermore, the results showed that ball motion affects the particle morphology, which changed from irregular type to plate type with increasing rotation speed. The evolution was also found to depend on the impact energy increase of the grinding media. These findings are useful to understand and optimize the particle motion and grinding behavior of traditional ball mills.

Flower-like nickel oxide (NiO) catalysts were coated on NiCrAl alloy foam using a hydrothermal method. The structural, morphological, and chemical bonding properties of the NiO catalysts coated on the NiCrAl alloy foam were investigated by field-emission scanning electron microscopy, scanning electron microscopy-energy dispersive spectroscopy, Xray diffraction, and X-ray photoelectron spectroscopy, respectively. To obtain flower-like morphology of NiO catalysts on the NiCrAl alloy foam, we prepared three different levels of pH of the hydrothermal solution: pH-7.0, pH-10.0, and pH-11.5. The NiO morphology of the pH-7.0 and pH-10.0 samples exhibited a large size plate owing to the slow reaction of the hydroxide (OH−) and nickel ions (Ni+) in lower pH than pH-11.5. Flower-like NiO catalysts (~4.7 μm-6.6 μm) were formed owing to the fast reaction of OH− and Ni2+ by increased OH− concentration at high pH. Thus, the flower-like morphology of NiO catalysts on NiCrAl alloy foam depends strongly on the pH of the hydrothermal solution.

연소화염법을 이용한 다이아몬드 박막합성시 기판표면온도 및 온도분포에 가장 크게 작용하는 공정변수는 탄화수소량을 결정하는 산소/아세틸렌 가스의 혼합비(R=O2C2H2)이다. 본 연구에서는 혼합가스비율 변화 (R=0.87-0.98)에 따른 기판표면온도 및 온도분포를 측정하고, 이들 변수에 따른 다이아몬드 박막의 생성 및 결정형상의 변화과정을 SEM관찰, Raman 분광분석 및 X-선 회절 분석을 통해 조사하였다. 혼합가스비율의 증가에 따라 다이아몬드의 생성입자 수밀도는 감소하였고, 이와 동시에 결정형상도 (111)면과 (100)면이 혼재된 cobo octahedron형에서 octahedron인 (111)면으로 변화되었다. 한편, 기판온도증가에 따라 생성입자의 수밀도가 증가하고 성장속도도 빨라져 조대한 결정을 얻었으며, 생성된 입자형성은 (111)면애 지배적이다가 (100)결정면이 점차 많아지는 양상을 나타내었다.

본 연구는 수면전개법으로 고분자 박막을 제조하기 위한 연구로서 PVC 및 CA의 고분자용액의 수면전개 거동과 생성된 박막의 구조특성을 검토하였다. 고분자용액의 수면전개성은 고분자용액의 용매선정에 따른 표면장력, 점도의 변화와 고분자의 농도변화에 따라 영향을 받았다. 또한 수면온도가 증가함에 따라 전개성은 저하되었다. 수면전개 박막의 구조는 고분자농도가 증가할수록 치밀하여 졌으며, 막의 응집상태는 공기면측과 수면측이 다르게 나타나 공기면측의 상태가 다소 치밀하였다. 또한 수면의 온도가 증가할수록 막의 구조는 더 치밀함을 보였다. 한편 3 wt.%의 CA용액으로부터 0.1μ의 두께를 갖는 박막을 얻었다.

본 연구에서는 프랙탈 이론의 하천유역분야 적용성을 고찰을 통하여 하상의 불연속 경계면을 보간하기 위한 침식모형기반 프랙탈 기법을 제시하고, 이를 이용하여 적용 대상인 하상 경계부분의 3차원 지형을 생성하여 실제 측량성과와의 비교, 공간 통계학적 분석을 통해 이론의 적용성을 검증하였다. 침식모형기반 프랙탈 기법의 검증을 위해 표본을 추출하여 실제 지형측량 결과 및 IDW 기법에 의한 보간 지형과의 분산분석을 수행하였다. 표본집단이 모집단과 동일 분산을 갖고 있는지에 대한 표고값 간의 F-검정 결과, 유의확률 0.501로 유의수준 0.05보다 큰 것으로 분석되어 표고의 표준차이는 없는 것으로 나타났다. 분산분석 결과 RMSE는 IDW 및 침식모형기반 프랙탈 기법 각 0.802, 0.384로 침식모형기반 프랙탈 기법이 우수한 것으로 나타났다. 이러한 결과로 부터 3차원 정밀 하상 지형 생성 방법으로 침식모형기반 프랙탈 기법의 적용성이 우수한 것으로 사료된다.