In this work, activated carbon nanofiber(ACNF) electrodes with high double-layer capaci-tance and good rate capability were prepared from polyacrylonitrile nanofibersby optimiz-ing the carbonization temperature prior to H2O activation. The morphology of the ACNFs was observed by scanning electron microscopy. The elemental composition was determined by analysis of X-ray photoelectron spectroscopy. N2-adsorption-isotherm characteristics at 77 K were confirmedby Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. ACNFs processed at different carbonization temperatures were applied as electrodes for electrical double-layer capacitors. The experimental results showed that the surface mor-phology of the CNFs was not significantlychanged after the carbonization process, although their diameters gradually decreased with increasing carbonization temperature. It was found that the carbon content in the CNFs could easily be tailored by controlling the carbonization temperature. The specificcapacitance of the prepared ACNFs was enhanced by increasing the carbonization temperature.

Well-distributed ruthenium (Ru) nanoparticles decorated on porous carbon nanofibers (CNFs) were synthesized using an electrospinning method and a reduction method for use in high-performance elctrochemical capacitors. The formation mechanisms including structural, morphological, and chemical bonding properties are demonstrated by means of field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). To investigate the optimum amount of the Ru nanoparticles decorated on the porous CNFs, we controlled three different weight ratios (0 wt%, 20 wt%, and 40 wt%) of the Ru nanoparticles on the porous CNFs. For the case of 20 wt% Ru nanoparticles decorated on the porous CNFs, TEM results indicate that the Ru nanoparticles with ~2-4 nm size are uniformly distributed on the porous CNFs. In addition, 40 wt% Ru nanoparticles decorated on the porous CNFs exhibit agglomerated Ru nanoparticles, which causes low performance of electrodes in electrochemical capacitors. Thus, proper distribution of 20 wt% Ru nanoparticles decorated on the porous CNFs presents superior specific capacitance (~280.5 F/g at 10 mV/s) as compared to the 40 wt% Ru nanoparticles decorated on the porous CNFs and the only porous CNFs. This enhancement can be attributed to the synergistic effects of well-distributed Ru nanoparticles and porous CNF supports having high surface area.

Activated carbon nanofibers(ACNF) were prepared from polyacrylonitrile (PAN)-based nanofibersusing CO2 activation methods with varying activation process times. The surface and structural characteristics of the ACNF were observed by scanning electron microscopy and X-ray diffraction, respectively. N2 adsorption isotherm characteristics at 77 K were con-firmedby Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. As experimental results, many holes or cavernous structures were found on the fibersurfaces after the CO2 activation as confirmedby scanning electron microscopy analysis. Specificsurface areas and pore volumes of the prepared ACNFs were enhanced within a range of 10 to 30 min of acti-vation times. Performance of the porous PAN-based nanofibersas an electrode for electrical double layer capacitors was evaluated in terms of the activation conditions.

Carbon nanofibers (CNFs) with diameters in the submicron and nanometer range exhibit high specific surface area, hierarchically porous structure, flexibility, and super strength which allow them to be used in the electrode materials of energy storage devices, and as hybrid-type filler in carbon fiber reinforced plastics and bone tissue scaffold. Unlike catalytic synthesis and other methods, electrospinning of various polymeric precursors followed by stabilization and carbonization has become a straightforward and convenient way to fabricate continuous CNFs. This paper is a comprehensive and brief review on the latest advances made in the development of electrospun CNFs with major focus on the promising applications accomplished by appropriately regulating the microstructural, mechanical, and electrical properties of as-spun CNFs. Additionally, the article describes the various strategies to make a variety of carbon CNFs for energy conversion and storage, catalysis, sensor, adsorption/separation, and biomedical applications. It is envisioned that electrospun CNFs will be the key materials of green science and technology through close collaborations with carbon fibers and carbon nanotubes.

In this study, activated carbons nanofibers (ACNFs) were prepared from polyacrylonitrile-based nanofibers by physical (H2O and CO2) and chemical (KOH) activation. The surface and structural characteristics of the porous carbon were observed by scanning electron microscopy and X-ray diffraction, respectively. Pore characteristics were investigated by N2/77K adsorption isotherms. The specific surface area of the physically ACNFs was increased up to 2400m2/g and the ACNFs were found to be mainly composed of micropore structures. Chemical activation using KOH produced ACNFs with high specific surface area (up to 2500m2/g), and the micropores were mainly found in the ACNFs. The physically and chemically ACNFs showed both mainly type I from the International Union of Pure and Applied Chemistry classification.

본 연구는 microfiltration (MF) 적용을 위한 PVdF/GO 하이브리드 나노섬유막(FG) 제조에 관한 것이다. 지지체인 PVdF (polyvinylidene difluoride) 나노섬유막은 N,N-Dimethylacetamide (DMAc)와 아세톤에 PVdF를 녹여 방사용액 제조 후 전기방사법을 이용하여 제조하였다. 본 연구에서 사용된 GO (grapheme oxide) sheets는 Hummer’s 방법에 따라 제조되었으며, PVdF 나노섬유 지지체 위에 에탄올에 분산시킨 GO용액을 분사함으로써, 최종적으로 PVdF/GO 하이브리드 나노섬유막(FG)을 제조하였다. FG막은 SEM, Raman, 접촉각, 기공특성분석장치(Porometer), 만능인장시험기(UTM)를 사용하여 조사하였고, 수투과도 분석은 제작된 셀(Dead-End Cell)을 이용하여 측정하였다. 접촉각 측정 결과로부터 제조된 FG막의 표면이 친수성으로 개질되었음을 확인할 수 있었으며, 수투과도값은 PVdF막에 비해 약 2.5배 향상된 것을 확인할 수 있었다.

In the present work, ZnO nanofibers were applied to electrode materials for the detection of cholesterol. ZnO nanofibers were synthesized using the electrospinning technique with zinc acetate as a precursor. Electrospinning-synthesized ZnO nanofibers were uniformly distributed by properly controlling the electrospinning parameters. After the calcination treatment, nanofibers of pure ZnO phase were synthesized. Then, these fibers were successfully placed on Au-coated glass substrates by dispersion of ZnO nanofibers in ethanol, dropping, and drying, in sequence. Cholesterol oxidase was then immobilized onto the surface of the ZnO nanofibers. To enhance the immobilization, Nafion was additionally applied. The sensing performances of the fabricated ZnO nanofibers-based sensors were analyzed by cyclic voltammetry in terms of cholesterol concentration ranging from 100 to 400 mg/dl. In the I-V curves, measured by cyclic voltammetry, the ZnO nanofiber-based sensor showed a proportional current behavior with cholesterol concentrations in phosphate buffered saline solution. The sensitivity was measured and found to be 30.7nA/mM·cm2, which is comparable to the values reported in the literature. After not only optimizing the shape of the ZnO nanofibers but also improving the adhesion nature between the ZnO nanofibers and the Au conducting layer, these fibers can be a good candidate for electrode materials in devices used to detect low concentrations of cholesterol in blood.

Polyacrylonitrile (PAN) 기질고분자를 용매인 dimethylformamide (DMF)에 녹인 후 전기방사법을 이용하여 polyacrylonitrile nanofibers membrane (PAM)을 제조하였으며, 정밀여과(microfiltration) 적용을 위해, 제조된 PAM 샘플들의 layer 수를 변화시켜, 기공크기를 조절하였다. 또한, 순수투과도(water-flux) 향상을 위해 poly (ethylene glycol) methyl ether methacrylate와 azobisisobutylronitrile (AIBN)을 이용하여 자유 라디칼 중합(free radical polymerization)을 통해 합성된 AN‐ PEGMA 공중합체를 PAN과 3:1의 비율로 혼합한 후 위와 같은 방법으로 다공성 막(PAM/APM)을 제조하였으며, FT-IR과 E.D.S 분석을 통해 PAM 샘플과 비교⋅분석하였다. Scanning Electron Microscope (SEM) 분석과 기공크기, 기공도 실험을 통해 균일한 직경(400∼600 nm)과 균일한 기공특성(0.5∼0.4 μm)을 가진 다공성 막이 제조되었음을 확인할 수 있었다. 순수 투과도 측정을 통해 정밀여과용 막으로의 활용가능성을 조사하였으며, AN‐PEGMA 공중합체가 도입된 PAM/APM의 경우 상 용막인 polyvinylidenefluoride (PVdF)에 비해 순수투과도가 상대적으로 높은 값을 나타내었다. 위의 결과로부터 전기방사법으로 제조된 PAN 나노섬유막들은 정밀여과용 막으로서 충분한 활용가능성이 있다고 판단된다.

Well-distributed SnO2-Sn-Ag3Sn nanoparticles embedded in carbon nanofibers were fabricated using a co-electrospinning method, which is set up with two coaxial capillaries. Their formation mechanisms were successfully demonstrated. The structural, morphological, and chemical compositional properties were investigated by field-emission scanning electron spectroscopy (FESEM), bright-field transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In particular, to obtain well-distributed SnO2 and Sn and Ag3Sn nanoparticles in carbon nanofibers, the relative molar ratios of the Ag precursor to the Sn precursor including 7 wt% polyacrylonitrile (PAN) were controlled at 0.1, 0.2, and 0.3. The FESEM, bright-field TEM, XRD, and XPS results show that the nanoparticles consisting of SnO2-Sn-Ag3Sn phases were in the range of ~4 nm-6 nm for sample A, ~5 nm-15 nm for sample B, ~9 nm-22 nm for sample C. In particular, for sample A, the nanoparticles were uniformly grown in the carbon nanofibers. Furthermore, when the amount of the Ag precursor and the Sn precursor was increased, the inorganic nanofibers consisting of the SnO2-Sn-Ag3Sn nanoparticles were formed due to the decreased amount of the carbon nanofibers. Thus, well-distributed nanoparticles embedded in the carbon nanofibers were successfully synthesized at the optimum molar ratio (0.1) of the Ag precursor to the Sn precursor after calcination of 800˚C.

We report on the NO gas sensing properties of non-directional ZnO nanofibers synthesized using a typical electrospinning technique. These non-directional ZnO nanofibers were electrospun on an SiO2/Si substrate from a solution containing poly vinyl alcohol (PVA) and zinc nitrate hexahydrate dissolved in distilled water. Calcination processing of the ZnO/PVA composite nanofibers resulted in a random network of polycrystalline ZnO nanofibers of 50 nm to 100 nm in diameter. The diameter of the nanofibers was found to depend primarily on the solution viscosity; a proper viscosity was maintained by adding PVA to fabricate uniform ZnO nanofibers. Microstructural measurements using scanning electron microscopy revealed that our synthesized ZnO nanofibers after calcination had coarser surface morphology than those before calcination, indicating that the calcination processing was sufficient to remove organic contents. From the gas sensing response measurements for various NO gas concentrations in dry air at several working temperatures, it was found that gas sensors based on electrospun ZnO nanofibers showed quite good responses, exhibiting a maximum sensitivity to NO gas in dry air at an operating temperature of 200˚C. In particular, the non-directional electrospun ZnO nanofiber gas sensors were found to have a good NO gas detection limit of sub-ppm levels in dry air. These results illustrate that non-directional electrospun ZnO nanofibers are promising for use in low-cost, high-performance practical NO gas sensors.

Metal nanowires can be coated on various substrates to create transparent conducting films that can potentially replace the dominant transparent conductor, indium tin oxide, in displays, solar cells, organic light-emitting diodes, and electrochromic windows. One issue with these metal nanowire based transparent conductive films is that the resistance between the nanowires is still high because of their low aspect ratio. Here, we demonstrate high-performance transparent conductive films with silver nanofiber networks synthesized by a low-cost and scalable electrospinning process followed by two-step sequential thermal treatments. First, the PVP/AgNO3 precursor nanofibers, which have an average diameter of 208 nm and are several thousands of micrometers in length, were synthesized by the electrospinning process. The thermal behavior and the phase and morphology evolution in the thermal treatment processes were systematically investigated to determine the thermal treatment atmosphere and temperature. PVP/AgNO3 nanofibers were transformed stepwise into PVP/Ag and Ag nanofibers by two-step sequential thermal treatments (i.e., 150˚C in H2 for 0.5 h and 300˚C in Ar for 3 h); however, the fibrous shape was perfectly maintained. The silver nanofibers have ultrahigh aspect ratios of up to 10000 and a small average diameter of 142 nm; they also have fused crossing points with ultra-low junction resistances, which result in high transmittance at low sheet resistance.

Poly-L-lactic acid (PLLA), PLLA/hydroxyapatite (HA), PLLA/multiwalled carbon nanotubes (MWNTs)/HA, PLLA/trifluoroethanol (TFE), PLLA/gelatin, and carbon nanofibers (CNFs)/β-tricalcium phosphate (β-TCP) composite membranes (scaffolds) were fabricated by electrospinning and their morphologies, and mechanical properties were characterized for use in bone tissue regeneration/guided tissue regeneration. MWNTs and HA nanoparticles were well distributed in the membranes and the degradation characteristics were improved. PLLA/MWNTs/HA membranes enhanced the adhesion and proliferation of periodontal ligament cells (PDLCs) by 30% and inhibited the adhesion of gingival epithelial cells by 30%. Osteoblast-like MG-63 cells on the randomly fiber oriented PLLA/TEF membrane showed irregular forms, while the cells exhibited shuttle-like shapes on the parallel fiber oriented membrane. Classical supersaturated simulated body fluids were modified by CO2 bubbling and applied to promote the biomineralization of the PLLA/gelatin membrane; this resulted in predictions of bone bonding bioactivity of the substrates. The β-TCP membranes exhibit good biocompatibility, have an effect on PDLC growth comparable to that of pure CNF membrane, and can be applied as scaffolds for bone tissue regeneration.

The oxyfluorination effects of activated carbon nanofibers (OFACFs) were investigated for CO2 storage. Electrospun CFs were prepared from a polyacrylonitrile/N,N-dimethylformamide solution via electrospinning and heat treatment. The electrospun CFs were chemically activated in order to generate the pore structure, and then oxyfluorination was used to modify the surface. The samples were labeled CF (electrospun CF), ACF (activated CF), OFACF-1 (O2:F2 = 7:3), OFACF-2 (O2:F2 = 5:5) and OFACF-3 (O2:F2 = 3:7). The functional group of OFACFs was investigated using X-ray photoelectron spectroscopy analysis. The C-F bonds formed on surface of ACFs. The intensities of the C-O peaks increased after oxyfluorination and increased the oxygen content in the reaction gas. The specific surface area, pore volume and pore size of OFACFs were calculated by the Brunauer-Emmett-Teller and density functional theory equation. Through the N2 adsorption isotherm, the specific surface area and pore volume slightly decreased as a result of oxyfluorination treatment. Nevertheless, the CO2 adsorption efficiency of oxyfluorinated ACF improved around 16 wt% due to the semi-ionic interaction effect of surface modificated oxygen functional groups and CO2 molecules.

Polyacrylonitrile-based carbon nanofibers (CNFs) containing Ti and Mn were prepared by electrospinning. The effect of metal content on the hydrogen storage capacity of the nanofibers was evaluated. The nanofibers containing Ti and Mn exhibited maximum hydrogen adsorption capacities of 1.6 and 1.1 wt%, respectively, at 303 K and 9 MPa. Toward the development of an improved hydrogen storage system, the optimum conditions for the production of metalized CNFs were investigated by characterizing the specific surface areas, pore volumes, sizes, and shapes of the fibers. According to the results of Brunauer-Emmett-Teller analysis, the activation of the CNFs using potassium hydroxide resulted in a large pore volume and specific surface area in the samples. This is attributable to the optimized pore structure of the metal-containing polyacrylonitrile-based electrospun CNFs, which may provide better sites for hydrogen adsorption than do current adsorbates.

In this work, graphite nanofibers (GNFs) were prepared by ammonia and heat treatment at temperatures up to 1000℃ to improve its CO2 adsorption capacity. The effects of the heat treatment on the textural properties and surface chemistry of the GNFs were investigated by N2 adsorption isotherms, XRD, and elemental analysis. We found that the chemical properties of GNFs were significantly changed after the ammonia treatment. Mainly amine groups were formed on the GNF surfaces such as lactam groups, pyrrole and pyridines. The GNFs treated at 500℃ showed highest CO2 adsorption capacity of 26.9 mg/g at 273 K in this system.

In this work, the effect of carbon nanofibers (CNFs) addition on physicochemical characteristics of CNFs-reinforced epoxy matrix nanocomposites was studied. Poly(amide imide) solutions in dimethylformamide were electrospun into webs consisting of 250±50 nm fibers which were used to produce CNFs through stabilization and carbonization processes. As a result, the CNFs with average diameter of 200±20 nm were obtained after carbonization process. The nanocomposites with CNFs showed an improvement of thermal stability parameters and fracture toughness factors, compared to those of the specimen without CNFs, which could be probably attributed to the higher specific surface area and larger aspect ratio of CNFs, resulting in improving the mechanical interlocking in the nanocomposites. Also, the applied external loading can effectively transfer to CNFs because strong interactions are resulted between the epoxy matrix and the CNFs.

In this study, porous electrospun carbon fibers were prepared by electrospinning with PAN and MgCl2, as a MgO precursor. MgO was selected as a substrate because of its chemical and thermal stability, no reaction with carbon, and ease of removal after carbonization by dissolving out in acidic solutions. MgCl2 was mixed with polyacrylonitrile (PAN) solution as a precursor of MgO with various weight ratios of MgCl2/PAN. The average diameter of porous electrospun carbon fibers increased from 1.3 to 3 μm, as the MgCl2 to PAN weight ratio increased. During the stabilization step, MgCl2 was hydrolyzed to MgOHCl by heat treatment. At elevated temperature of 823 K for carbonization step, MgOHCl was decomposed to MgO. Specific surface area and pore structure of prepared electrospun carbon fibers were decided by weight ratio of MgCl2/PAN. The amount of hydrogen storage increased with increase of specific surface area and micropore volume of prepared electrospun carbon fibers.

Carbon nanofiber (CNF) grown catalytically was chemically activated with KOH to attain structural change of CNF. The structural changes of CNF through KOH activation were investigated by using BET and SEM. From the results of BET, it was found that KOH activation was effective to develop particular sizes of pores on the CNF surface, increasing the surface area of CNF. Activated CNF was applied as an anode catalyst support of fuel cell. The effects of different activation conditions including the activation temperature and the activation time on the specific surface area of the CNF activated with KOH were investigated to obtain appropriate structure as a catalyst support. The 60 wt% Pt-Ru catalyst prepared was observed by using TEM and XRD.