We present a high-performance polymeric membrane based on self-cross-linkable poly(glycidyl methacrylate-g-poly-(propylene glycol))-co-poly(oxyethylene methacrylate) (PGP-POEM) graft copolymer for CO2/N2 separation. The self-cross-linked membranes can be easily prepared under mild conditions without any additional cross-linking agents or catalyst. We investigated the gas separation performance of the membranes as a function of POEM content in the copolymer. The self-cross-linked PGP-POEM membranes showed an improvement in both permeance and selectivity with increasing POEM content up to 51.2 wt %. The best performance of the membrane was achieved by optimizing membrane thickness, showing a CO2 permeance of 500 GPU (1 GPU = 10-6 cm3 (STP)/(s cm2 cmHg)) and CO2/N2 selectivity of 22.4.

무분별한 이산화탄소 배출로 인한 지구온난화는 이상기후와 생태계 파괴 등을 초래함으로써 인간의 삶에 심각한 영향을 미치고 있다. 이러한 문제의 근본 원인인 이산화탄소 배출을 저감하는 방법으로 본 연구에서는 자가-가교 성질이 있는 P(GMA-g-PPG)-co-POEM) (SP) 공중합체와 상용 고분자인 polyvinylpyrrolidone (PVP)를 혼합하여 블렌드 고분자 분리막을 제조하는 방법을 제시하였다. PVP 함량에 따른 분리막의 이산화탄소/질소 투과 특성을 확인하였으며, PVP의 함량이 증가 할수록 투과도는 감소하고 선택도는 증가하는 결과를 보였다. 특히 PVP 함량이 30 wt%인 경우, 투과도는 순수 SP 고분자의 CO2 투과도인 72.9 GPU에서 12.6 GPU로 감소하였으나, CO2/N2 선택도는 28.1에서 50.4로 약 79% 증가하였다. 이는 SP 공중합체와 PVP 사이의 수소결합으로 인해 고분자 사슬이 더욱 조밀하게 배열되기 때문인 것으로 볼 수 있으며, 이를 FT-IR, TGA, XRD, SEM을 통해 분석하였다. 따라서, 본 연구에서는 SP/PVP 고분자 블렌드 내 PVP의 함량을 조절함으로써 분리막의 투과도 및 선택도를 손쉽게 조절할 수 있음을 확인하였다.