We report on stretchable electrochromic films of poly(3-hexylthiophene) (P3HT) fabricated on silver nanowire (AgNW) electrodes. AgNWs electrodes are prepared on polydimethylsiloxane (PDMS) substrates using a spray coater for stretchable electrochromic applications. On top of the AgNW electrode, poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) is introduced to ensure a stable resistance over the electrode under broad strain range by effectively suppressing the protrusion of AgNWs from PDMS. This bilayer electrode exhibits a high performance as a stretchable substrate in terms of sheet resistance increment by a factor of 1.6, tensile strain change to 40%, and stretching cycles to 100 cycles. Furthermore, P3HT film spin-coated on the bilayer electrode shows a stable electrochromic coloration within an applied voltage, with a color contrast of 28.6%, response time of 4-5 sec, and a coloration efficiency of 91.0 cm2/C. These findings indicate that AgNWs/PEDOT:PSS bilayer on PDMS substrate electrode is highly suitable for transparent and stretchable electrochromic devices.

고성능 투명 전극의 개발은 유기 태양 전지, 유기 발광 다이오드와 같은 저가형 유연 유기 광전자 소자의 개발에 매우 중요하다. 가장 널리 쓰이고 있는 투명전극인 indium tin oxide (ITO)는 비싼 가격과 잘 깨어지는 특성 을 가지고 있어서 저가형 유연 전자 소자의 개발에 많은 제한을 주고 있으며, 이를 극복하기 위한 대체 투명 전극의 개발에 대한 연구가 활발히 진행되고 있다. 은 나노와이어(silver nanowire, AgNW)는 우수한 전기 전도도와 광 투과 도를 가지고 저렴하며 뛰어난 유연성 때문에 ITO의 대체 투명전극으로서 큰 각광을 받고 있다. 그러나 AgNW의 거 친 표면은 유기 광전자 소자의 누설전류를 크게 증가시켜서 소자의 효율을 떨어뜨리기 때문에 이를 극복하는 기술의 개발이 시급한 실정이다. 본 연구에서는 UV 광 경화성 접착제를 이용하여 AgNW를 PET기판으로 transfer 시키는 방법으로 AgNW가 매몰된 유연 전도성 투명 기판을 제작하였으며, 이 기판은 낮은 표면 거칠기, 낮은 면저항과 높은 광투과도를 보여준다. 본 연구에서 개발된 AgNW가 매몰된 유연 전도성 투명 기판은 유기전자소자의 대체투명전극 으로 활용될 수 있는 가능성을 보여준다.