Recently, scaling of pavement concrete is becoming problem by excessive use of deicer. The current study measured durability of concrete not considering multi-deterioration using design and construction mixing used general concrete pavement.

Domestic portland cement(OPC) is made up of clinker, gypsum and 5% of admixtures. If 5% of Admixture contents of portland cement add to 10%, CO2 reduction effect can be expected. In this study, Freezing and Thawing test of concrete using limestone powder was evaluated.

In this study, performance of the post-installed anchor system was evaluated with reduced strength of concrete and anchor. One of the post-installed anchors was selected to performance evaluation. Concrete strength was reduced by freeze-thawing test, and the post-installed anchor strength was reduced by corrosion test. The post-installed Anchor was installed in concrete of freezing and thawing and original concrete, and corroded anchor was installed in original concrete only. Anchor diameter and installation depth of the anchor were the variable for each specimen. Performance of post-installed anchor system of each specimen was evaluated by pullout test. Anchor diameter and installation depth of anchor, it may affect the performance of the post-installed anchor system from the experimental test results. Fracture mode of each post-installed anchor system had occurred differently depending on the durability of concrete and anchor. The anchor pullout strength from the experimental test results was used in order to compare with the results of CCD (Concrete Capacity Design) method, and CCD equation was modified. Modified equation was able to predict the anchor pullout strength of post-installed anchor system in Original concrete and freezing and thawing of concrete.

Ground granulated blast furnace slag is known to be much less quality variation compared to the fly ash can be substituted. Have high salt damage resistance, and chemical resistance of concrete with ground granulated blast furnace slag substitution. The case of NPP concrete using fly ash in concrete, and is defined as less than 20% fly ash utilization. In this paper, consider a resistance to freezing-thawing of currently used to concrete in NPP structures and substitutes for ground granulated blast furnace slag

원형 구조물의 보수/보강 및 FRP를 구조부재로 활용한 신설 구조물 시공을 위해서는 일정한 곡률반경을 갖는 곡면 FRP 부재가 요구된다. 그러나 현재까지 FRP 곡면부재는 수작업 (hand-lay-up) 또는 필라멘트 와인딩 (filament winding) 작업에 의해서만 생산이 가능하였으며, 대량 연속생산에는 한계가 있다. 또한 일반적으로 인발성형법 (pultrusion method)으로 생산된 FRP 부재가 상대적으로 물리적 특성이 우수한 것으로 알려져 있다. 따라서 FRP 부재를 일정곡률을 유지하며 인발로 뽑아낼 수 있는 신개념의 곡면 FRP 부재 인발성형법 제안 및 성형장비를 개발, 곡면 FRP 제품을 생산하였으며, 본 연구에서는 곡면 FRP 부재를 이용한 구조물 보수/보강시 야기될 수 있는 FRP와 콘크리트 부착면의 동결융해 영향을 분석하였다.

콘크리트 구조물은 일반적으로 동결융해 작용을 받는 조건에 노출되고, 이러한 동결융해작용은 콘크리트의 공극구조를 변화시키고, 콘크리트의 내구성을 저하시킬 우려가 있다. 따라서 본 연구에서는 동결융해작용에 의한 콘크리트 내부공극구조 변화와 동결융해작용을 받은 콘크리트의 내구특성을 평가하고자 하였다. 실험결과, 기존의 동결융해 평가기법에 따르면 모든 배합에서 우수한 내구성능을 나타내었으나, 동결융해 작용에 노출됨에 따라 50~100nm 크기의 공극이 크게 증가하며, 콘크리트 염화물침투저항성이 저하하였다. 수중양생 콘크리트의 공극구조와 염화물 침투저항성은 선형관계를 보이지만, 동결융해작용을 받으면 내부공극구조의 변화로 선형관계가 저하하였다. 동결융해작용과 염화물침투를 동시에 받는 구조물의 내구성 평가기준에 대한 재검토가 필요할 것으로 판단된다.

Human embryonic stem cells (hESCs) are promising cell source because of their unique self-renewal and pluripotency. Although hESC-derived cardiac cells are currently generated worldwide, cryopreservation of these cells is still limited due to low rate of post-thaw survival. Cryopreservation of hESC-derived cardiac cells is critical in that their long-term storage can accelerate their use in regenerative medicine. However, to date, there are few reports on efficient cryopreservation and post-thaw survival of hESC-derived cardiac cells. In this study, we evaluated the effects of ginsenoside, which is known to improve survival of rat embryonic cardiomyocytes against myocardial ischemia injury in diabetic rats (Wu et al., 2011), on the survival of hESC-derived cardiac cells after thawing. We induced differentiation into cardiac cells using our previously reported method (Kim et al., 2011). Differentiated, pre-beating stage cardiac cells were cryopreserved using either mass cryopreservation or vitrification. To evaluate the effects of ginsenoside (Re, Rb), we compared three sets: pre- and post-thaw treatment, pre- or post-thaw treatment only. The survival of post-thaw cardiac cells were evaluated using Trypan-blue and Annexin V staining. In addition, the three groups were treated with ROCK inhibitor Y-27632, and compared with non-treatment groups. The effect of ginsenoside was significant in post-thaw treatment group, i.e, thawed cells expressed cardiac specific genes and showed specific functionality such as spontaneous beating. Taken together, we demonstrated favorable effects of ginsenoside on the survival of hESC-derived cardiac cells after cryopreservation and thawing. These results suggest a possible application of well-known cardioprotectant ginsenoside in cell-based tissue engineering using hESC-derived cardiac cells.

The sensory properties of Kalopanax pictus and Cedrela sinensis shoots were analyzed according to their blanching conditions and the thawing methods used. For the Hunter colors, the K. pictus that was blanched without adding salt for 6 min had the highest L value, and the C. sinensis that was blanched with 1% salt for 6 min had the highest L value. The chlorophyll content of K. pictus was 141.1 mg% when it was blanched for 3 min with 2% salt, and the chlorophyll content of C. sinensis that was blanched without adding salt for 6 min was highest (124.8 mg%). When K. pictus and C. sinensis were blanched without salt addition for 3 min, their texture showed a higher value than that of the other samples. The sensory test result showed the highest overall preference for the sample that was blanched without adding salt for 3 min, among all the samples. The L value of the K. pictus that was thawed in a microwave oven was significantly higher than that of the other samples, but the L value of the C. sinensis that was thawed at 4℃ was higher than that of the other samples. As for the overall preference for the samples according to the thawing method used, K. pictus and C. sinensis scored highest in the case of thawing in a microwave oven.

2002년에 백두산 지역을 중심으로 강진에 의한 지표면 팽창현상이 관찰되면서, 백두산의 화산폭발 가능성이 높아지고 있다. 이에 따라, 그동안 국내에서 재난유형으로 별도의 분류가 없던 화산폭발에 대한 대책이 정부차원에서 논의되기 시작하였다. 화산폭발이 발생하면 무수한 화산재가 각종 사회기반시설을 덮게 되며, 비산에 의해 항공, 물류, 정밀기계산업 등에 타격이 발생하게 된다. 본 연구에서는 화산재를 건설재료로 활용하기 위하여 백두산, 한라산의 화산재 및 다공성의 제올라이트에 시멘트 및 메타카올린을 첨가한 재령 7일의 공시체에 대한 배합비별 동결융해 저항성을 분석하였다. 실험 결과, 재령 7일에 대하여 혼합재(화산재 및 제오라이트), 시멘트 및 메타카올린의 비율을 3.5：1：0.1로 배합한 경우 동결융해 저항성이 가장 우수한 것으로 나타나, 재령 및 단위시멘트량의 증가, 메타카올린의 첨가가 동결융해 저항성에 큰 영향을 미치는 것으로 나타났다.

본 연구는 오가피순과 두릅의 소비 확대와 가공품 개발의 전처리로 필수적인 blanching 조건을 설정하기 위해 blanching 온도와 식염의 농도에 따른 품질 변화와 관능적 특성을 평가하고자 하였다. 또한 해동조건에 따른 이화학적 및 관능적 특성을 평가하여 오가피순과 두릅의 품질을 향상시킬 수 해동조건을 설정하고자 하였다. Blanching은 식염 첨가량(무첨가, 1%, 2% 첨가)과 blanching 시간(4분, 7분)을 달리하였으며, 해동

본 논문에서는 FRP 복합체로 보강된 콘크리트 구조물의 동결융해 저항성을 평가하기 위하여 동결융해 진행에 따른 FRP 복합체의 인장강도 및 콘크리트에 대한 인발접착강도의 변화를 측정하였다. 주 실험변수는 동결융해 조건, FRP 복합체의 종류, 동결융해 싸이클로 설정하였다. KS F 2456의 동결융해 시험규격에 따라 실시된 탄소섬유복합체의 인장강도는 최종 싸이클까지 변화가 없었으며, 또한 접착성능의 저하도 관측되지 않아 CFRP의 동결융해 저항성은 매우 우수한 것으로 나타났다. 이에 대하여 유리섬유복합체의 경우는 최종 싸이클에서의 인장강도 및 인발접착강도가 각각 10%, 15% 저하된 것으로 나타나 부분적으로 성능이 저하되는 것으로 나타났다. 그러나 접착강도 평가시 지속적인 동결수가 공급되는 상황에서는 상이한 결과가 나타날 수 있으므로 이에 대한 주의가 필요할 것으로 판단된다.

일반적으로 철근콘크리트 건축물은 외부의 기후에 노출되어 있어 겨울에서 이른 봄까지 동결과 융해의 반복적인 작용에 영향을 받는다. 이러한 동결융해 작용은 콘크리트의 균열을 발생시키거나 콘크리트 표면의 박리를 일으켜 내구성 저하의 원인이 된다. 본 연구에서는 철근콘크리트 보의 동결융해 노출에 따른 휨 거동특성의 평가를 위해 주근비와 동결융해 사이클을 변수로 하였다. -18~4℃의 온도범위에서 150 및 300 사이클의 동결융해에 노출시킨 실험체를 비롯하여 14개의 축소모형 실험체를 제작, 단조 및 반복하중 하에서 실험을 실시하였다. 실험결과를 통해 동결융해에 노출되어있는 철근콘크리트 보의 휨 거동특성을 평가하는데 기초적인 자료를 제시하고자 하였다

건축물의 보수․보강 시 섬유보강 폴리머를 이용한 부착공법을 이용한 보수․보강이 행해지고 있으며, 특히 CFRP(carbon fiber reinforced polymer)는 이러한 RC 구조부재의 보강재로 널리 활용되고 있다. 그러나 외부 환경적 요인에 의해 열화되는 즉, 동결융해 환경이 RC 보에서의 CFRP 보강성능에 미치는 영향에 관한 연구는 전무한 실정이다. 따라서 본 연구에서는 AE 기법을 통해 CFRP와 RC 부재 내부의 손상진전에 따라 발생하는 AE 신호를 계측함으로써 CFRP로 보강 후 동결융해에 의해 열화된 RC 구조물의 파괴기구 규명을 위한 기초자료를 마련하고자 한다.

마쇄 홍고추를 -70, 에서 품온이 에 도달할 때까지 냉동하여 저장고에서 한 달간 저장한 후 온도(0, )와 조건(수침지식, 공기 해동법)을 달리 하여 해동한 후 성분을 비교.분석하였다. Capsaicin과 dihydrocapsaicin 함량은 각각 4.28, 2.69 mg/100 g으로 해동 후 , /100 g 으로 감소하였으며 처리구가 감소하여 가장 큰 변화를 나타내었다. 비타민 C 함량 또한 에서의 감소가 가장 컸으며 처리구에서

본 연구에서는 염화물이 함유된 동결수에 의한 콘크리트의 내동해성을 검토하기 위하여 동결융해 및 표면스케일링 저항성을 평가하고자 하였으며, 이를 위한 배합으로서 물결합재비는 0.37, 0.42, 0.47의 3수준, 결합재 방식은 일반 OPC 콘크리트, 고로슬래그 미분말 50%의 2성분계 콘크리트 및 플라이애시 15%와 고로슬래그 미분말 35%의 3성분계 콘크리트로 설정하였다. 그 결과, 고로슬래그 미분말 50% 및 플라이애시 15%와 고로슬래그 미분말 35%의 혼합 시멘트계 콘크리트의 경우 일반 OPC 콘크리트에 비하여 동결융해 및 표면스케일링 저항성이 상대적으로 우수하게 나타났으며, 이를 통해 내구성 저하가 우려되는 해양 환경 하에서 비래염분 및 비말 등의 해수의 작용에 의한 콘크리트의 내구성 저하현상을 억제하기 위한 방안으로서 슬래그의 활용이 유효함을 확인할 수 있었다.

홍고추를 원료형태에 따라 원형, 세절, 분쇄로 제조하여 및 저장고에 보관하였다. 고추의 표면색도는 저장온도 조건에 따라 저장일수가 증가할수록 약간 감소하는 경향을 보였으며, 비타민 C 함량은 원형 홍고추가 세절고추나 분쇄고추보다 저장기간 동안 완만하게 감소하는 경향을 보였다. 저장온도별로는 저장군에서 비타민 C 함량이 가장 높게 유지되었으며, 저장군에서 저장 2개월째 50% 이하로 급격히 감소하였다. 유리당 함량은 저장일수가 증가할수록

컴퓨터 세포동결기를 이용하여 생쥐 배아를 동결할 때 액체질소 (L)의 분사속도가 해빙 후 배아의 미세구조, 기능 및 발달에 미치는 영향을 알아보고자 하였다. 이를 위해 배아는 동결을 하지 않은 대조군 (control) 및 동결군에서 L의 분사속도에 따라 고속분사군 (120 infusion/min group 1), 저속분사군 (50 infusion/min; group 2)으로 나누었다. ICR 계열의 생쥐의 2 세포기 배아를 사용하였으며, 동결 및 해빙은