2219 aluminum alloy bonded diamond wheels containing intermetallic compounds were fabricated by powder metallurgy method. Nickel and titanium were added in aluminum matrix piece. The hot pressing condition was and 20 Mpa in the furnace of the electric resistance type. The mechanical properties and grinding tests were carried out to confirm the wheel performance. Aluminum oxide ceramics were chosen for use in the grinding tests. The test proved that the heat resistance 2219 aluminum bonded diamond wheel containing 15 wt% nickel and 15 wt% titanium respectively showed the best performance.