A capsule is the device for irradiation test of nuclear materials and fuels in HANARO. The instrumentation cables are sealed tightly by brazing at the top of the capsule. In this study, the integrities at the brazing of both Inconel 600 and STS 310 materials were confirmed by tensile test, survey of damage on coating, and measurement of insulation resistance. At tensile test, brazing areas were not damaged but the thermocouples themselves were broken on both the materials. At flame heat test, the coating of STS 310 material was maintained without damage but the brittle fracture on Inconel 600 material was observed. Insulation resistances were confirmed to be satisfactory in case of both the materials. In this analysis, the thermocouple was expanded by 0.81mm on the direction of y-axis and the tube was contracted by 0.57mm on the direction of x-axis. As the result, cracks might be occurred with thermal stresses. EDX spectrum analysis showed that the BAg-1 filler metal formed a thin reaction layer on the surface of brazed metal.
1. 서론
2. 실험방법
2.1 사용재료
2.2 브레이징 방법
3. 실험 결과
3.1 기계적 특성
3.2 열전대 피복 특성
3.3 절연저항 특성
3.4 재료 응력특성 해석
3.5 브레이징 접합면의 특성
4. 결론
참고문헌