In order to reduce the sintering temperature of iron based sintered parts, sinteing properties of iron-copper prealloyed powder were investigated at various temperatures in the range of 700∼890, and than the rusults were compared with those of the conventional iron-copper-tin compact using elemental powders, The using of prealloyed as a new process improved its sintering performance at lower temperature than elemental powder as the conventional process. The relative sintered density and radial crushing stength of the compact using prealloyed were higher than those of using elemental powder at all sintering temperature. For example, the radial curength of the compact using powder was about 50kg/mm2 at 700, while that of the compact using elemental powder sintered at 890 was 43kg/mm2.