A process has been successfully used to manufacture 6061/Graphite composite material and the Graphite particles are distributed uniformly within the Al alloy matrix. The 6061 powders was mixed with natural Graphite particles in a ball milling blender and cold compacted specimens were extruded into rods 15mm in diameter at 450. The results showed that tensile properties of the composites with Graphite content have been reduced. The emergence of fine microstructures appeared to be related to the graphite volume. Heat-treated composites were found to possess good mechanical properties as compared with those of non heated composites. A model was used that the tensile strength of the composites would be estimated from the theoretical calculation and experimental data.

• 김홍물