fine powder was synthesized by hydrothermal process from the mixture of titania-hydroxide() and barium hexa-hydroxide () as starting materials. Fine powder(< 100 nm) was made under the reaction conditions of 18,10 atm, 1.5 hr in autoclave and showed cubic structure. The powders were sintered by a spark plasma sintering technique from 1050~115 for 5 min. The grains of sample sintered at 110 were about 0.9 in average size and showed the mixture of cubic and tetragonal structures.