The effects of mechanical alloying conditions on the formation of Mn-sulfide powders were analyzed. Impeller rotating speed, lubricant coating and added amounts of process control agent(stearic acid) were selected as a process control factor. MnS compounds are synthesized in 3 hours by mechanical alloying at the alternative milling condition. Discontinuous rotating speed of 1200rpm for 4 minutes and 1000rpm for 1 minute shows more effects on the compound formation of MnS. After coating of lubricant on the wall, elementary Mn and sulfur were partially remained by mechanical alloying. The friction effects of the wall and grinding media on the powders are significantly important to form the compound of MnS.