기계적 합금화에 의한 Ti-37.5at%Si 분말의 합성 및 소결 특성 KCI 등재
The Synthesis of Ti-37.5at%Si Powders by MA and Their Sintering Characteristics
- 언어KOR
- URLhttps://db.koreascholar.com/Article/Detail/2201
pp.223-230
Ti-37.5at%Si elemental powder mixtures were mechanically alloyed by a high-energy ball mill, followed by CIP (cold isostatic pressing) and HIP (hot isostatic pressing) for different processing conditions. Only elemental phases (Ti and Si) were observed for the 5 min mechanically alloyed (MA 5 min) powder, but only phase was observed for the 30 min mechanically alloyed (MA 30 min) powder. phase was observed for the HIPed compact of MA 5 min and 30 min powders at 150 and 190 MPa for 3 hr at . For the HIPed compacts, the highest sintered density was obtained to be 99.5% of theoretical density by a HIP step at at 190MPa for 3hr. The hardness values of the HIPed compacts at at 150/190 MPa for 3hr were higher than HRC 76. The densification and mechanical property of HIPed compacts was found to depend on more HIP temperature than HIP pressure.