To investigate the fabrication possibility of a polymer particle dispersed metal matrix composite, polytetrafluorothylene (PTFE) particles were incorporated into the Al by the powder metallurgy process. The characteristics of a PTFE/Al composite were evaluated by measuring the density and hardness, and analysis of XRD, FT-Raman and microstructure. And wear properties of these composites were evaluated under the dry wear condition. It was possible to obtain the PTFE particles stably dispersed Al matrix composites by the hot press process at the sintering temperature of . The wear coefficient of a PTFE/Al compoite decreased with increasing of the volume fraction of PTFE. The wear weight of a PTFE/Al composite increased with increasing of the volume fractionof PTFE in the range of 0~10 vol.%PTFE, and showed maximum value at 10 vol.%PTFE, and then decreased at 20vol.%PTFE.

• 이길근
• 김우열