FePt nanoparticles for high-density magnetic recording media were synthesized by the simultaneous chemical reduction of Fe(acac) and Pt(acac) with 1,2-hexadecanediol as the reducing reagent. TEM images showed that the shape of as-synthesized FePt nanoparticle was spherical and average particle size was 3 nm. Also, SAD pattern showed that crystal structure was disordered FCC (face centered cubic). These FCC structured nanoparticles were transformed FCT (face centered tetragonal) structure by annealing at 55 for 30 min in Ar atmosphere. XRD analysis revealed that as-synthesized FePt nanoparticles were transformed from disordered FCC to ordered FCT. Finally, the coercivity of 2 kOe for FePt nanoparticles with FCT structure was obtained by VSM measurement.