The present work investigated the dispersion behavior of Y2O3 particles into AISI 316L SS manufactured using laser cladding technology. The starting particles were produced by high energy ball milling in 10 min for pre- alloying, which has a trapping effect and homogeneous dispersion of Y2O3 particles, followed by laser cladding using CO2 laser source. The phase and crystal structures of the cladded alloys were examined by XRD, and the cross section was characterized using SEM. The detailed microstructure was also studied through FE-TEM. The results clearly indi- cated that as the amount of Y2O3 increased, micro-sized defects consisted of coarse Y2O3 were increased. It was also revealed that homogeneously distributed spherical precipitates were amorphous silicon oxides containing yttrium. This study represents much to a new technology for the manufacture and maintenance of ODS alloys.

• 박은광(Dept. of Metallurgical Engineering, Jeonbuk National University, Nuclear Materials Development Division, Korea Atomic Energy Research Institute (KAERI)) | Eun-Kwang Park
• 홍성모(Nuclear Materials Development Division, Korea Atomic Energy Research Institute (KAERI), Division of Advanced Materials Engineering, Kongju National University) | Sung-Mo Hong
• 박진주(Nuclear Materials Development Division, Korea Atomic Energy Research Institute (KAERI)) | Jin-Ju Park Corresponding Author
• 이민구(Nuclear Materials Development Division, Korea Atomic Energy Research Institute (KAERI)) | Min-Ku Lee
• 이창규(Nuclear Materials Development Division, Korea Atomic Energy Research Institute (KAERI)) | Chang-Kyu Rhee
• 설경원(Dept. of Metallurgical Engineering, Jeonbuk National University) | Kyeong-won Seol
• 이양규(Dept. of Management Information System, Seowon University) | Yang-Kyu Lee