In this paper, the I-resistance curve of low-carbon steel with 3 mm thickness was investigated for various crack ratios. The experiments were carried out for the center cracked tension (CCT) specimen with about 50 mm width on an instron machine. The plane stress fracture toughness obtained by the Simpson's formula was Ii. = 24.96 kgffmm. Simpson's formula which considers crack growth in obtaining J integral showed more conservative lin than Rice's and Sumpter's. For materials that may be approximated by the Ramberg and Osgood stress strain law, the relevant crack parameters like the J integral, load line displacement are approximately normalized. Crack driving forces in terms of the I integral are computed for low-carbon steel CCT specimen using the above estimation scheme. Comparison of the prediction with actual experimental measurements by Simpson's formula showed good agreement for several different sized specimen.