In order to study a reversible photoisomerization of disperse red l(DR 1) attached on natural polymers, cellulose acetate containing DR l(DR 1/CA adduct) was prepared, and the changes of UV/VIS spectra of its solution(benzene, DMAc). thick film, and LB film were investigated by alternate irradiation with two different wave length lights. DR 1/CA adduct was prepared through tosylation of partially hydrolyzed cellulose acetate followed by reaction with DR 1 at 100℃ in pyridine. From the UV/VIS spectra of DR 1/CA adduct dissolved in DMAc solvent including phosphoglyceride before and after irradiation at 360nm and 45Onm, we found out the changes of UV/VIS spectra were reversible. In addition, the change of UV/VIS spectra of this adduct solution was strongly depended on the sorts of solvents and temperature. As the temperature was increased, UV/VIS spectra of this adduct solution in DMF showed blue shift. These results provided this solution could be applied to a temperature sensor. In the thick film case, we also obtained similar results with solution case. LB monolayer and trilayer from DR 1/CA adduct was obtained by scattering the solution including phosphoglyceride on water surface at the surface pressure of 8mN/m. After irradiation on that LB monolayer and trilayer, the reversible photoisomerization was also detected. From these results we concluded DR 1/CA adduct was suitable for the application to data storage and optical switch, etc.